- 密度 [g/cm3]: 1.43
- 吸水率 [%]: 0.3
- 缺口冲击强度: 0.163
- 弯曲强度 [MPa]: 64.0
- 弯曲模量 [MPa]: 7.40
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.660 g/cc | 0.0238 lb/in³ | ASTM D1895 |
| Density | 1.43 g/cc | 0.0517 lb/in³ | ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 88 | 88 | ASTM D785 |
| Tensile Strength, Ultimate | 64.0 MPa | 9280 psi | ASTM D638 |
| Elongation at Break | 0.92 % | 0.92 % | ASTM D638 |
| Tensile Modulus | 8.70 GPa | 1260 ksi | ASTM D638 |
| Flexural Strength | 95.0 MPa | 13800 psi | ASTM D790 |
| Flexural Modulus | 7.40 GPa | 1070 ksi | ASTM D790 |
| Compressive Strength | 208 MPa | 30200 psi | ASTM D695 |
| Izod Impact, Notched | 0.163 J/cm | 0.305 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.184 J/cm² | 0.876 ft-lb/in² | ASTM D256 |
| Impact | 99 | 99 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.60e+11 ohm-cm | 2.60e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.7 | 5.7 | ASTM D150 |
| Dielectric Strength | 9.10 kV/mm | 231 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.050 | 0.050 | ASTM D150 |
| Arc Resistance | 25 sec | 25 sec | ASTM D495 |
| Comparative Tracking Index | 200 V | 200 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 52.0 µm/m-°C @Temperature 40.0 - 130 °C | 28.9 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.440 W/m-K @Temperature 100 °C | 3.05 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 200 °C | 392 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C | 315 °F | ASTM D648 |
| Oxygen Index | 28.3 % | 28.3 % | ASTM D2863 |
| Shrinkage | 0.30 % | 0.30 % | 72 hr, 120ºC; ASTM D1299 |