- 密度 [g/cm3]: 1.76
- 吸水率 [%]: 0.101
- 缺口冲击强度: 0.38
- 弯曲强度 [MPa]: 92.0
- 弯曲模量 [MPa]: 14.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.700 g/cc | 0.0253 lb/in³ | ASTM D1895 |
| Density | 1.76 g/cc | 0.0636 lb/in³ | ASTM D792 |
| Water Absorption | 0.101 % | 0.101 % | ASTM D570 |
| Linear Mold Shrinkage | 0.00116 cm/cm | 0.00116 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 99 | 99 | ASTM D785 |
| Tensile Strength, Ultimate | 92.0 MPa | 13300 psi | ASTM D638 |
| Elongation at Break | 0.85 % | 0.85 % | ASTM D638 |
| Tensile Modulus | 14.3 GPa | 2070 ksi | ASTM D638 |
| Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
| Flexural Modulus | 14.5 GPa | 2100 ksi | ASTM D790 |
| Compressive Strength | 243 MPa | 35200 psi | ASTM D695 |
| Poissons Ratio | 0.31 | 0.31 | ASTM D638 |
| Shear Modulus | 5.46 GPa | 792 ksi | Calculated |
| Izod Impact, Notched | 0.380 J/cm | 0.712 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.370 J/cm² | 1.76 ft-lb/in² | ASTM D256 |
| Impact | 230 | 230 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 6.60e+11 ohm-cm | 6.60e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.1 | 5.1 | ASTM D150 |
| Dielectric Strength | 17.1 kV/mm | 434 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.033 | 0.033 | ASTM D150 |
| Arc Resistance | 136 sec | 136 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 35.0 µm/m-°C @Temperature 40.0 - 130 °C | 19.4 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Maximum Service Temperature, Air | 196 °C | 385 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 224 °C | 435 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | |
| Oxygen Index | 35 % | 35 % | ASTM D2863 |
| Shrinkage | 0.043 % | 0.043 % | 72 hr, 120ºC; ASTM D1299 |