- 密度 [g/cm3]: 1.45
- 吸水率 [%]: 0.267
- 缺口冲击强度: 0.166
- 弯曲强度 [MPa]: 61.0
- 弯曲模量 [MPa]: 7.60
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.650 g/cc | 0.0235 lb/in³ | ASTM D1895 |
| Density | 1.45 g/cc | 0.0524 lb/in³ | ASTM D792 |
| Water Absorption | 0.267 % | 0.267 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0083 cm/cm | 0.0083 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 82 | 82 | ASTM D785 |
| Tensile Strength, Ultimate | 61.0 MPa | 8850 psi | ASTM D638 |
| Elongation at Break | 0.91 % | 0.91 % | ASTM D638 |
| Tensile Modulus | 8.50 GPa | 1230 ksi | ASTM D638 |
| Flexural Strength | 93.0 MPa | 13500 psi | ASTM D790 |
| Flexural Modulus | 7.60 GPa | 1100 ksi | ASTM D790 |
| Compressive Strength | 189 MPa | 27400 psi | ASTM D695 |
| Poissons Ratio | 0.35 | 0.35 | ASTM D638 |
| Shear Modulus | 3.15 GPa | 457 ksi | Calculated |
| Izod Impact, Notched | 0.166 J/cm | 0.311 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.178 J/cm² | 0.847 ft-lb/in² | ASTM D256 |
| Impact | 100 | 100 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 8.00e+10 ohm-cm | 8.00e+10 ohm-cm | ASTM D247 |
| Dielectric Constant | 10.2 | 10.2 | ASTM D150 |
| Dissipation Factor | 0.061 | 0.061 | ASTM D150 |
| Arc Resistance | 137 sec | 137 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 46.0 µm/m-°C @Temperature 40.0 - 130 °C | 25.6 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.510 W/m-K @Temperature 100 °C | 3.54 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 201 °C | 394 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 155 °C | 311 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | |
| Oxygen Index | 27.5 % | 27.5 % | ASTM D2863 |
| Shrinkage | 0.269 % | 0.269 % | 72 hr, 120ºC; ASTM D1299 |