- 密度 [g/cm3]: 1.77
- 吸水率 [%]: 0.099
- 缺口冲击强度: 0.34
- 弯曲强度 [MPa]: 78.0
- 弯曲模量 [MPa]: 12.7
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.720 g/cc | 0.0260 lb/in³ | ASTM D1895 |
| Density | 1.77 g/cc | 0.0639 lb/in³ | ASTM D792 |
| Water Absorption | 0.099 % | 0.099 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0031 cm/cm | 0.0031 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 96 | 96 | ASTM D785 |
| Tensile Strength, Ultimate | 78.0 MPa | 11300 psi | ASTM D638 |
| Elongation at Break | 0.77 % | 0.77 % | ASTM D638 |
| Tensile Modulus | 13.3 GPa | 1930 ksi | ASTM D638 |
| Flexural Strength | 131 MPa | 19000 psi | ASTM D790 |
| Flexural Modulus | 12.7 GPa | 1840 ksi | ASTM D790 |
| Compressive Strength | 214 MPa | 31000 psi | ASTM D695 |
| Izod Impact, Notched | 0.340 J/cm | 0.637 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.296 J/cm² | 1.41 ft-lb/in² | ASTM D256 |
| Impact | 177 | 177 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 5.30e+11 ohm-cm | 5.30e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.0 | 5.0 | ASTM D150 |
| Dielectric Strength | 8.40 kV/mm | 213 kV/in | Step by Step; ASTM D149 |
| 20.9 kV/mm | 531 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.033 | 0.033 | ASTM D150 |
| Arc Resistance | 159 sec | 159 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 35.0 µm/m-°C @Temperature 40.0 - 130 °C | 19.4 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.540 W/m-K @Temperature 100 °C | 3.75 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 194 °C | 381 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 196 °C | 385 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | |
| Oxygen Index | 34 % | 34 % | ASTM D2863 |
| Shrinkage | 0.084 % | 0.084 % | 72 hr, 120ºC; ASTM D1299 |