- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 0.59
- 缺口冲击强度: 0.247
- 弯曲强度 [MPa]: 50.0
- 弯曲模量 [MPa]: 6.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.480 g/cc | 0.0173 lb/in³ | ASTM D1895 |
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 |
| Water Absorption | 0.59 % | 0.59 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0098 cm/cm | 0.0098 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 81 | 81 | ASTM D785 |
| Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
| Elongation at Break | 0.71 % | 0.71 % | ASTM D638 |
| Tensile Modulus | 7.60 GPa | 1100 ksi | ASTM D638 |
| Flexural Strength | 67.0 MPa | 9720 psi | ASTM D790 |
| Flexural Modulus | 6.10 GPa | 885 ksi | ASTM D790 |
| Compressive Strength | 182 MPa | 26400 psi | ASTM D695 |
| Poissons Ratio | 0.34 | 0.34 | ASTM D638 |
| Shear Modulus | 2.84 GPa | 412 ksi | Calculated |
| Izod Impact, Notched | 0.247 J/cm | 0.463 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.222 J/cm² | 1.06 ft-lb/in² | ASTM D256 |
| Impact | 191 | 191 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.50e+11 ohm-cm | 1.50e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.1 | 5.1 | ASTM D150 |
| Dielectric Strength | 7.20 kV/mm | 183 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.064 | 0.064 | ASTM D150 |
| Arc Resistance | 110 sec | 110 sec | ASTM D495 |
| Comparative Tracking Index | 150 V | 150 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 52.0 µm/m-°C @Temperature 40.0 - 130 °C | 28.9 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Maximum Service Temperature, Air | 180 °C | 356 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 147 °C | 297 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 6.00 mm | V-0 @Thickness 0.236 in | |
| Oxygen Index | 25.6 % | 25.6 % | ASTM D2863 |
| Shrinkage | 0.48 % | 0.48 % | 72 hr, 120ºC; ASTM D1299 |