- 密度 [g/cm3]: 1.45
- 吸水率 [%]: 0.18
- 缺口冲击强度: 0.26
- 断裂伸长率 [%]: 76.4
- 弯曲强度 [MPa]: 50.8
- 弯曲模量 [MPa]: 7.62
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.550 g/cc | 0.0199 lb/in³ | Apparent density per ASTM D1895 |
| Water Absorption | 0.18 % | 0.18 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | per ATM D955. Post shrinkage is 0.22% per ASTM D1299. |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 91 | 91 | ASTM D785 |
| Tensile Strength, Ultimate | 50.8 MPa | 7370 psi | ASTM D638 |
| Elongation at Break | 0.75 % | 0.75 % | ASTM D638 |
| Tensile Modulus | 7.85 GPa | 1140 ksi | ASTM D638 |
| Flexural Yield Strength | 76.4 MPa | 11100 psi | ASTM D790 |
| Flexural Modulus | 7.62 GPa | 1110 ksi | ASTM D790 |
| Compressive Yield Strength | 213 MPa | 30900 psi | ASTM D695 |
| Poissons Ratio | 0.35 | 0.35 | In tension |
| Shear Modulus | 2.91 GPa | 422 ksi | Calculated |
| Izod Impact, Notched | 0.260 J/cm | 0.487 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ASTM D256 |
| Impact | 153 | 153 | J/m Plenco drop ball test |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.44e+11 ohm-cm | 1.44e+11 ohm-cm | ASTM D257 |
| Dielectric Constant | 5.8 @Frequency 1e+6 Hz | 5.8 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 8.80 kV/mm | 224 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.071 @Frequency 1e+6 Hz | 0.071 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 160 sec | 160 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 35.0 µm/m-°C @Temperature 20.0 °C | 19.4 µin/in-°F @Temperature 68.0 °F | |
| Maximum Service Temperature, Air | 200 °C | 392 °F | Heat resistance per ASTM D794 |
| Deflection Temperature at 1.8 MPa (264 psi) | 183 °C | 361 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.47 mm | HB @Thickness 0.0579 in | |