- 密度 [g/cm3]: 1.58
- 吸水率 [%]: 0.15
- 断裂伸长率 [%]: 84.0
- 弯曲强度 [MPa]: 51.8
- 弯曲模量 [MPa]: 9.08
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.670 g/cc | 0.0242 lb/in³ | Apparent density per ASTM D1895 |
| Water Absorption | 0.15 % | 0.15 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0058 cm/cm | 0.0058 in/in | per ATM D955. Post shrinkage is 0.15% at 72hr 120ºC per ASTM D1299. |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 82 | 82 | ASTM D785 |
| Tensile Strength, Ultimate | 51.8 MPa | 7510 psi | ASTM D638 |
| Elongation at Break | 0.59 % | 0.59 % | ASTM D638 |
| Tensile Modulus | 10.08 GPa | 1462 ksi | ASTM D638 |
| Flexural Yield Strength | 84.0 MPa | 12200 psi | ASTM D790 |
| Flexural Modulus | 9.08 GPa | 1320 ksi | ASTM D790 |
| Compressive Yield Strength | 191.6 MPa | 27790 psi | ASTM D695 |
| Poissons Ratio | 0.33 | 0.33 | In tension |
| Shear Modulus | 3.80 GPa | 551 ksi | Calculated |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | ASTM D256 |
| Impact | 122 | 122 | J/m Plenco drop ball test |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 4.01e+11 ohm-cm | 4.01e+11 ohm-cm | ASTM D257 |
| Dielectric Constant | 5.0 @Frequency 1e+6 Hz | 5.0 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 12.2 kV/mm | 310 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.049 @Frequency 1e+6 Hz | 0.049 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 180 sec | 180 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 30.0 µm/m-°C @Temperature 20.0 °C | 16.7 µin/in-°F @Temperature 68.0 °F | |
| Maximum Service Temperature, Air | 203 °C | 397 °F | Heat resistance per ASTM D794 |
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.47 mm | V-0 @Thickness 0.0579 in | |