- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 0.4
- 缺口冲击强度: 0.192
- 弯曲强度 [MPa]: 53.0
- 弯曲模量 [MPa]: 6.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.550 g/cc | 0.0199 lb/in³ | ASTM D1895 |
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0079 cm/cm | 0.0079 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 84 | 84 | ASTM D785 |
| Tensile Strength, Ultimate | 53.0 MPa | 7690 psi | ASTM D638 |
| Elongation at Break | 0.82 % | 0.82 % | ASTM D638 |
| Tensile Modulus | 7.50 GPa | 1090 ksi | ASTM D638 |
| Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
| Flexural Modulus | 6.80 GPa | 986 ksi | ASTM D790 |
| Compressive Strength | 194 MPa | 28100 psi | ASTM D695 |
| Izod Impact, Notched | 0.192 J/cm | 0.360 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.199 J/cm² | 0.947 ft-lb/in² | ASTM D256 |
| Impact | 118 | 118 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.80e+11 ohm-cm | 2.80e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 4.9 | 4.9 | ASTM D150 |
| Dielectric Strength | 10.9 kV/mm | 277 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.054 | 0.054 | ASTM D150 |
| Arc Resistance | 133 sec | 133 sec | ASTM D495 |
| Comparative Tracking Index | 150 V | 150 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 60.0 µm/m-°C @Temperature 40.0 - 130 °C | 33.3 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Maximum Service Temperature, Air | 200 °C | 392 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| Shrinkage | 0.267 % | 0.267 % | 72 hr, 120ºC; ASTM D1299 |