- 密度 [g/cm3]: 0.27
- 断裂伸长率 [%]: 26.0
- 弯曲强度 [MPa]: 17.0
- 弯曲模量 [MPa]: 1.27
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.270 - 1.71 g/cc | 0.00975 - 0.0618 lb/in³ | Average value: 0.767 g/cc Grade Count:9 |
| Linear Mold Shrinkage | 0.000500 - 0.100 cm/cm | 0.000500 - 0.100 in/in | Average value: 0.0248 cm/cm Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 17.0 - 303 MPa | 2470 - 43900 psi | Average value: 115 MPa Grade Count:6 |
| Elongation at Break | 1.70 - 11.0 % | 1.70 - 11.0 % | Average value: 4.25 % Grade Count:4 |
| Flexural Yield Strength | 26.0 - 432 MPa | 3770 - 62700 psi | Average value: 190 MPa Grade Count:6 |
| Flexural Modulus | 1.27 - 15.0 GPa | 184 - 2180 ksi | Average value: 6.70 GPa Grade Count:6 |
| Compressive Yield Strength | 4.80 - 6.00 MPa | 696 - 870 psi | Average value: 5.40 MPa Grade Count:3 |
| Compressive Modulus | 0.104 - 0.155 GPa | 15.1 - 22.5 ksi | Average value: 0.133 GPa Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 14.0 - 26.0 µm/m-°C | 7.78 - 14.4 µin/in-°F | Average value: 17.8 µm/m-°C Grade Count:5 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 - 213 °C | 158 - 415 °F | Average value: 173 °C Grade Count:4 |