- 弯曲强度 [MPa]: 32.4
- 热变形温度 [℃]: 73.9
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | |||
| Brookfield Viscosity | 550 cP | 550 cP | Part B | ||
| 650 cP | 650 cP | Mixed | |||
| 600 cP @Temperature 25.0 °C | 600 cP @Temperature 77.0 °F | Part A | |||
| Linear Mold Shrinkage | 0.00030 cm/cm | 0.00030 in/in | ASTM D2566 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 82 @Temperature 23.9 °C | 82 @Temperature 75.0 °F | ASTM D2240-68 | ||
| Tensile Strength, Ultimate | 32.4 MPa | 4700 psi | ASTM D638-82 | ||
| Elongation at Break | 7.0 - 10 % | 7.0 - 10 % | ASTM D790 | ||
| Tensile Modulus | >= 0.621 GPa | >= 90.0 ksi | 5% strain; ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 73.9 °C | 165 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 360 - 480 min @Temperature 24.0 °C | 6.00 - 8.00 hour @Temperature 75.2 °F | demold time | ||
| 7200 - 10080 min @Temperature 24.0 °C | 120 - 168.0 hour @Temperature 75.2 °F | full cure | |||
| Pot Life | 12 - 14 min @Temperature 24.0 °C | 12 - 14 min @Temperature 75.2 °F | mass dependent | ||
| Descriptive Properties | |||||
| Mix Ratio | 100:85 by weight, 100:88 by volume, resin/harder | ||||