- 密度 [g/cm3]: 1.17
- 吸水率 [%]: 3.3
- 弯曲强度 [MPa]: 45.0
- 热变形温度 [℃]: 67.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | |
| Water Absorption | 3.3 % | 3.3 % | Saturation in water |
| Water Absorption at Saturation | 3.3 % | 3.3 % | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | |
| Elongation at Break | 23 % | 23 % | |
| Tensile Modulus | 1.30 GPa | 189 ksi | |
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 9.00e+13 ohm-cm | 9.00e+13 ohm-cm | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | |
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 135 µm/m-°C @Temperature 20.0 °C | 75.0 µin/in-°F @Temperature 68.0 °F | in flow direction |
| CTE, linear, Transverse to Flow | 135 µm/m-°C @Temperature 20.0 °C | 75.0 µin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | |
| Vicat Softening Point | 94.0 °C | 201 °F | |