| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 0.0120 cP @Temperature 160 °C | 0.0120 cP @Temperature 320 °F | Rheology, 2°C/min | ||
| 0.0300 cP @Temperature 80.0 °C | 0.0300 cP @Temperature 176 °F | Rheology, 2°C/min | |||
| 0.100 cP @Temperature 120 °C | 0.100 cP @Temperature 248 °F | Rheology, 2°C/min | |||
| 7.00 cP @Temperature 40.0 °C | 7.00 cP @Temperature 104 °F | Rheology, 2°C/min | |||
| 105 cP @Temperature 175 °C | 105 cP @Temperature 347 °F | Rheology, 2°C/min | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 6.89 MPa | 1000 psi | Flatwise, 90 min @ 350°F, Spring Clamp Pressure, Abraded 6061-T6 Untreated; ASTM C297M | ||
| Shear Strength | 10.34 MPa @Temperature 177 °C | 1500 psi @Temperature 350 °F | 2 hr soak, 90 min @ 350°F, Spring Clamp Pressure, FPL Acid Etched 6061-T6; ASTM D1002 | ||
| 20.68 MPa @Temperature 177 °C | 3000 psi @Temperature 350 °F | 90 min @ 350°F, Spring Clamp Pressure, FPL Acid Etched 6061-T6; ASTM D1002 | |||
| 26.20 MPa @Temperature 121 °C | 3800 psi @Temperature 250 °F | 90 min @ 350°F, Spring Clamp Pressure, FPL Acid Etched 6061-T6; ASTM D1002 | |||
| 28.96 MPa @Temperature 21.1 °C | 4200 psi @Temperature 70.0 °F | 90 min @ 350°F, Spring Clamp Pressure, FPL Acid Etched 6061-T6; ASTM D1002 | |||
| Peel Strength | 2.98 kN/m @Temperature 21.1 °C | 17.0 pli @Temperature 70.0 °F | T-Peel, 90 min @ 350°F, Spring Clamp Pressure, FPL Acid Etched 6061-T6; ASTM D1876 | ||
| 4.56 kN/m @Temperature 121 °C | 26.0 pli @Temperature 250 °F | T-Peel, 90 min @ 350°F, Spring Clamp Pressure, FPL Acid Etched 6061-T6; ASTM D1876 | |||
| 5.61 kN/m @Temperature 177 °C | 32.0 pli @Temperature 350 °F | Roller Peel, 90 min @ 350°F, Spring Clamp Pressure, FPL Acid Etched 6061-T6; ASTM D3167 | |||
| 6.49 kN/m @Temperature 21.1 °C | 37.0 pli @Temperature 70.0 °F | Roller Peel, 90 min @ 350°F, Spring Clamp Pressure, FPL Acid Etched 6061-T6; ASTM D3167 | |||
| 7.54 kN/m @Temperature 121 °C | 43.0 pli @Temperature 250 °F | Roller Peel, 90 min @ 350°F, Spring Clamp Pressure, FPL Acid Etched 6061-T6; ASTM D3167 | |||
| Descriptive Properties | |||||
| Drum Peel | 19.8 in-lb/in | Tool Side Up, 2 hrs @ 250°F, 30 psi, 6061 T6 Abraded, 1” Nomex 3 lb core 1/8” cell | |||
| 20.5 in-lb/in | Tool Side Down, 2 hrs @ 250°F, 30 psi, 6061 T6 Abraded, 1” Nomex 3 lb core 1/8” cell | ||||
| Load to Failure | 606 lbf | 5 lb Core, 6 hrs @ 220°F, Vacuum Bag | |||
| 669 lbf | 8 lb Core, 6 hrs @ 220°F, Vacuum Bag | ||||