- 熔体流动速率 [g/10min]: 14.0
- 密度 [g/cm3]: 1.22
- 吸水率 [%]: 0.03
- 缺口冲击强度: 0.03
- 拉伸强度 [MPa]: 45.0
- 断裂伸长率 [%]: 81.0
- 弯曲强度 [MPa]: 45.0
- 弯曲模量 [MPa]: 2.20
- 硬度: 119.0
- 热变形温度 [℃]: 124.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 - 1.81 g/cc | 0.0441 - 0.0654 lb/in³ | Average value: 1.56 g/cc Grade Count:21 |
| Water Absorption | 0.0300 - 0.0700 % | 0.0300 - 0.0700 % | Average value: 0.0478 % Grade Count:9 |
| Moisture Absorption at Equilibrium | 0.0300 - 0.420 % | 0.0300 - 0.420 % | Average value: 0.133 % Grade Count:7 |
| Water Absorption at Saturation | 0.0700 - 0.420 % | 0.0700 - 0.420 % | Average value: 0.133 % Grade Count:7 |
| Linear Mold Shrinkage | 0.00200 - 0.0190 cm/cm | 0.00200 - 0.0190 in/in | Average value: 0.00700 cm/cm Grade Count:20 |
| Linear Mold Shrinkage, Transverse | 0.00400 - 0.0130 cm/cm | 0.00400 - 0.0130 in/in | Average value: 0.00912 cm/cm Grade Count:11 |
| Melt Flow | 14.0 - 64.0 g/10 min | 14.0 - 64.0 g/10 min | Average value: 37.4 g/10 min Grade Count:12 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 90.0 - 95.0 | 90.0 - 95.0 | Average value: 93.3 Grade Count:6 |
| Hardness, Rockwell R | 119 - 120 | 119 - 120 | Average value: 120 Grade Count:5 |
| Tensile Strength, Ultimate | 45.0 - 145 MPa | 6530 - 21000 psi | Average value: 83.3 MPa Grade Count:20 |
| Tensile Strength, Yield | 45.0 - 145 MPa | 6530 - 21000 psi | Average value: 88.5 MPa Grade Count:9 |
| Elongation at Break | 1.50 - 118 % | 1.50 - 118 % | Average value: 9.75 % Grade Count:19 |
| Elongation at Yield | 1.50 - 5.00 % | 1.50 - 5.00 % | Average value: 2.25 % Grade Count:8 |
| Modulus of Elasticity | 2.28 - 15.0 GPa | 331 - 2180 ksi | Average value: 8.79 GPa Grade Count:12 |
| Flexural Yield Strength | 81.0 - 220 MPa | 11700 - 31900 psi | Average value: 137 MPa Grade Count:21 |
| Flexural Modulus | 2.20 - 12.2 GPa | 319 - 1770 ksi | Average value: 7.32 GPa Grade Count:21 |
| Compressive Yield Strength | 54.0 - 103 MPa | 7830 - 14900 psi | Average value: 83.3 MPa Grade Count:6 |
| Izod Impact, Notched | 0.0300 - 8.17 J/cm | 0.0562 - 15.3 ft-lb/in | Average value: 1.10 J/cm Grade Count:21 |
| 0.0300 - 2.47 J/cm @Temperature -30.0 - -30.0 °C | 0.0562 - 4.63 ft-lb/in @Temperature -22.0 - -22.0 °F | Average value: 0.672 J/cm Grade Count:9 | |
| Izod Impact, Unnotched | 4.31 - 8.27 J/cm | 8.07 - 15.5 ft-lb/in | Average value: 6.83 J/cm Grade Count:8 |
| Izod Impact, Notched (ISO) | 2.00 - 62.0 kJ/m² | 0.952 - 29.5 ft-lb/in² | Average value: 9.60 kJ/m² Grade Count:10 |
| 2.00 - 18.0 kJ/m² @Temperature -30.0 - -30.0 °C | 0.952 - 8.57 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 5.56 kJ/m² Grade Count:9 | |
| Charpy Impact, Notched | 0.100 - 1.80 J/cm² | 0.476 - 8.57 ft-lb/in² | Average value: 0.763 J/cm² Grade Count:8 |
| 0.200 - 0.200 J/cm² @Temperature -30.0 - -30.0 °C | 0.952 - 0.952 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 0.200 J/cm² Grade Count:1 | |
| Dart Drop, Total Energy | 4.00 - 55.0 J | 2.95 - 40.6 ft-lb | Average value: 10.9 J Grade Count:10 |
| Taber Abrasion, mg/1000 Cycles | 15.0 - 74.0 | 15.0 - 74.0 | Average value: 32.6 Grade Count:7 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+16 - 1.80e+16 ohm-cm | 1.00e+16 - 1.80e+16 ohm-cm | Average value: 1.20e+16 ohm-cm Grade Count:8 |
| Dielectric Constant | 3.60 - 3.80 | 3.60 - 3.80 | Average value: 3.72 Grade Count:3 |
| Dielectric Strength | 18.8 - 25.0 kV/mm | 478 - 635 kV/in | Average value: 23.2 kV/mm Grade Count:8 |
| Dissipation Factor | 0.00200 - 0.0150 | 0.00200 - 0.0150 | Average value: 0.00683 Grade Count:3 |
| Arc Resistance | 60.0 - 130 sec | 60.0 - 130 sec | Average value: 99.8 sec Grade Count:8 |
| Comparative Tracking Index | 175 - 475 V | 175 - 475 V | Average value: 257 V Grade Count:9 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 14.4 - 90.0 µm/m-°C | 8.00 - 50.0 µin/in-°F | Average value: 38.9 µm/m-°C Grade Count:14 |
| 21.6 - 21.6 µm/m-°C @Temperature 60.0 - 138 °C | 12.0 - 12.0 µin/in-°F @Temperature 140 - 280 °F | Average value: 21.6 µm/m-°C Grade Count:2 | |
| CTE, linear, Transverse to Flow | 59.4 - 90.0 µm/m-°C | 33.0 - 50.0 µin/in-°F | Average value: 67.5 µm/m-°C Grade Count:11 |
| Melting Point | 255 °C | 491 °F | Average value: 255 °C Grade Count:6 |
| Deflection Temperature at 0.46 MPa (66 psi) | 124 - 225 °C | 255 - 437 °F | Average value: 205 °C Grade Count:19 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 - 218 °C | 149 - 424 °F | Average value: 150 °C Grade Count:21 |
| Vicat Softening Point | 130 - 221 °C | 266 - 430 °F | Average value: 180 °C Grade Count:12 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:9 |