- 熔体流动速率 [g/10min]: 0.88
- 密度 [g/cm3]: 1.3
- 吸水率 [%]: 0.02
- 缺口冲击强度: 0.32
- 断裂伸长率 [%]: 105
- 弯曲强度 [MPa]: 70.0
- 弯曲模量 [MPa]: 5.00
- 硬度: 118.0
- 热变形温度 [℃]: 182.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 - 1.75 g/cc | 0.0470 - 0.0632 lb/in³ | Average value: 1.42 g/cc Grade Count:37 |
| Filler Content | 3.00 - 50.0 % | 3.00 - 50.0 % | Average value: 19.4 % Grade Count:12 |
| Water Absorption | 0.0200 - 0.100 % | 0.0200 - 0.100 % | Average value: 0.0905 % Grade Count:21 |
| Additive Loading | 30.0 % | 30.0 % | Average value: 30.0 % Grade Count:3 |
| Linear Mold Shrinkage | 0.000500 - 0.0150 cm/cm | 0.000500 - 0.0150 in/in | Average value: 0.00366 cm/cm Grade Count:34 |
| Melt Flow | 0.880 - 56.4 g/10 min | 0.880 - 56.4 g/10 min | Average value: 21.7 g/10 min Grade Count:9 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 118 - 121 | 118 - 121 | Average value: 119 Grade Count:4 |
| Tensile Strength, Ultimate | 70.0 - 165 MPa | 10200 - 24000 psi | Average value: 121 MPa Grade Count:35 |
| Elongation at Break | 0.500 - 6.00 % | 0.500 - 6.00 % | Average value: 2.53 % Grade Count:22 |
| Elongation at Yield | 0.800 - 4.50 % | 0.800 - 4.50 % | Average value: 2.36 % Grade Count:15 |
| Modulus of Elasticity | 6.00 - 40.0 GPa | 870 - 5800 ksi | Average value: 14.2 GPa Grade Count:33 |
| Flexural Yield Strength | 105 - 248 MPa | 15200 - 36000 psi | Average value: 178 MPa Grade Count:36 |
| Flexural Modulus | 5.00 - 27.6 GPa | 725 - 4000 ksi | Average value: 11.4 GPa Grade Count:36 |
| Izod Impact, Notched | 0.320 - 2.14 J/cm | 0.600 - 4.00 ft-lb/in | Average value: 0.650 J/cm Grade Count:20 |
| Izod Impact, Unnotched | 3.74 - 6.94 J/cm | 7.00 - 13.0 ft-lb/in | Average value: 4.70 J/cm Grade Count:17 |
| Izod Impact, Notched (ISO) | 4.00 - 7.00 kJ/m² | 1.90 - 3.33 ft-lb/in² | Average value: 5.33 kJ/m² Grade Count:3 |
| 6.00 - 6.00 kJ/m² @Temperature -30.0 - -30.0 °C | 2.86 - 2.86 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 6.00 kJ/m² Grade Count:1 | |
| Izod Impact, Unnotched (ISO) | 25.0 - 45.0 kJ/m² | 11.9 - 21.4 ft-lb/in² | Average value: 33.3 kJ/m² Grade Count:3 |
| 40.0 - 40.0 kJ/m² @Temperature -30.0 - -30.0 °C | 19.0 - 19.0 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 40.0 kJ/m² Grade Count:1 | |
| Charpy Impact Unnotched | 2.00 - 4.50 J/cm² | 9.52 - 21.4 ft-lb/in² | Average value: 3.21 J/cm² Grade Count:14 |
| 4.00 - 4.00 J/cm² @Temperature -30.0 - -30.0 °C | 19.0 - 19.0 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 4.00 J/cm² Grade Count:1 | |
| Coefficient of Friction | 0.140 - 0.240 | 0.140 - 0.240 | Average value: 0.190 Grade Count:5 |
| Coefficient of Friction, Static | 0.100 - 0.190 | 0.100 - 0.190 | Average value: 0.148 Grade Count:5 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 10.0 - 1.00e+9 ohm-cm | 10.0 - 1.00e+9 ohm-cm | Average value: 6.00e+7 ohm-cm Grade Count:17 |
| Surface Resistance | 10.0 - 1.00e+12 ohm | 10.0 - 1.00e+12 ohm | Average value: 4.04e+10 ohm Grade Count:23 |
| Insulation Resistance | 10.0 - 1.00e+10 ohm | 10.0 - 1.00e+10 ohm | Average value: 7.22e+8 ohm Grade Count:14 |
| Static Decay | 2.00 sec | 2.00 sec | Average value: 2.00 sec Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 16.0 - 48.6 µm/m-°C | 8.89 - 27.0 µin/in-°F | Average value: 25.1 µm/m-°C Grade Count:4 |
| Melting Point | 225 - 227 °C | 437 - 441 °F | Average value: 227 °C Grade Count:4 |
| Maximum Service Temperature, Air | 120 - 180 °C | 248 - 356 °F | Average value: 151 °C Grade Count:14 |
| Deflection Temperature at 0.46 MPa (66 psi) | 182 - 224 °C | 360 - 435 °F | Average value: 200 °C Grade Count:6 |
| Deflection Temperature at 1.8 MPa (264 psi) | 171 - 226 °C | 340 - 438 °F | Average value: 200 °C Grade Count:15 |
| Vicat Softening Point | 205 - 215 °C | 401 - 419 °F | Average value: 211 °C Grade Count:5 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:20 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 232 - 270 °C | 450 - 518 °F | Average value: 249 °C Grade Count:19 |
| Nozzle Temperature | 250 - 265 °C | 482 - 509 °F | Average value: 258 °C Grade Count:14 |
| Melt Temperature | 238 - 280 °C | 460 - 536 °F | Average value: 259 °C Grade Count:27 |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | Average value: 91.5 °C Grade Count:32 |
| Drying Temperature | 80.0 - 121 °C | 176 - 250 °F | Average value: 107 °C Grade Count:28 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.90 hour Grade Count:10 |
| Moisture Content | 0.0300 - 0.0800 % | 0.0300 - 0.0800 % | Average value: 0.0336 % Grade Count:14 |
| Dew Point | -28.9 °C | -20.0 °F | Average value: -28.9 °C Grade Count:13 |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | Average value: 86.2 MPa Grade Count:17 |