- 熔体流动速率 [g/10min]: 9.5
- 密度 [g/cm3]: 1.22
- 吸水率 [%]: 0.08
- 缺口冲击强度: 0.481
- 拉伸强度 [MPa]: 35.0
- 断裂伸长率 [%]: 78.5
- 弯曲强度 [MPa]: 34.0
- 弯曲模量 [MPa]: 0.196
- 硬度: 79.0
- 热变形温度 [℃]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 - 1.45 g/cc | 0.0441 - 0.0524 lb/in³ | Average value: 1.32 g/cc Grade Count:30 |
| Water Absorption | 0.0800 - 0.600 % | 0.0800 - 0.600 % | Average value: 0.391 % Grade Count:16 |
| Moisture Absorption at Equilibrium | 0.0800 - 0.200 % | 0.0800 - 0.200 % | Average value: 0.175 % Grade Count:16 |
| Viscosity Test | 105 - 158 cm³/g | 105 - 158 cm³/g | Average value: 137 cm³/g Grade Count:5 |
| Linear Mold Shrinkage | 0.00160 - 0.0230 cm/cm | 0.00160 - 0.0230 in/in | Average value: 0.00963 cm/cm Grade Count:12 |
| Linear Mold Shrinkage, Transverse | 0.00160 - 0.0160 cm/cm | 0.00160 - 0.0160 in/in | Average value: 0.00390 cm/cm Grade Count:7 |
| Melt Flow | 9.50 - 236 g/10 min | 9.50 - 236 g/10 min | Average value: 41.6 g/10 min Grade Count:18 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 79.0 - 119 | 79.0 - 119 | Average value: 108 Grade Count:5 |
| Tensile Strength, Ultimate | 34.0 - 68.0 MPa | 4930 - 9860 psi | Average value: 55.1 MPa Grade Count:14 |
| Tensile Strength, Yield | 35.0 - 62.0 MPa | 5080 - 8990 psi | Average value: 52.4 MPa Grade Count:19 |
| Elongation at Break | 2.90 - 300 % | 2.90 - 300 % | Average value: 70.8 % Grade Count:29 |
| Elongation at Yield | 2.90 - 8.00 % | 2.90 - 8.00 % | Average value: 4.71 % Grade Count:17 |
| Modulus of Elasticity | 1.70 - 2.86 GPa | 247 - 415 ksi | Average value: 2.49 GPa Grade Count:19 |
| Flexural Yield Strength | 78.5 - 94.0 MPa | 11400 - 13600 psi | Average value: 82.1 MPa Grade Count:6 |
| Flexural Modulus | 0.196 - 2.55 GPa | 28.4 - 370 ksi | Average value: 2.06 GPa Grade Count:12 |
| Izod Impact, Notched | 0.481 - 0.800 J/cm | 0.900 - 1.50 ft-lb/in | Average value: 0.540 J/cm Grade Count:6 |
| Izod Impact, Notched (ISO) | 7.00 - 7.00 kJ/m² @Temperature -30.0 - -30.0 °C | 3.33 - 3.33 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 7.00 kJ/m² Grade Count:1 |
| Izod Impact, Unnotched (ISO) | NB - NB @Temperature -30.0 - -30.0 °C | NB - NB @Temperature -22.0 - -22.0 °F | Grade Count:1 |
| Charpy Impact Unnotched | 13.5 J/cm² - NB | 64.2 ft-lb/in² - NB | Average value: 16.8 J/cm² Grade Count:15 |
| 12.0 J/cm² - NB @Temperature -30.0 - -30.0 °C | 57.1 ft-lb/in² - NB @Temperature -22.0 - -22.0 °F | Average value: 18.3 J/cm² Grade Count:14 | |
| Charpy Impact, Notched | 0.160 - 7.50 J/cm² | 0.761 - 35.7 ft-lb/in² | Average value: 1.35 J/cm² Grade Count:19 |
| 0.500 - 2.50 J/cm² @Temperature -30.0 - -30.0 °C | 2.38 - 11.9 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 1.08 J/cm² Grade Count:13 | |
| Puncture Energy | 14.7 - 44.0 J | 10.8 - 32.5 ft-lb | Average value: 31.1 J Grade Count:6 |
| 2.00 - 32.0 J @Temperature -30.0 - -30.0 °C | 1.48 - 23.6 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 17.6 J Grade Count:5 | |
| Tensile Creep Modulus, 1 hour | 1400 - 2400 MPa | 203000 - 348000 psi | Average value: 2120 MPa Grade Count:9 |
| Tensile Creep Modulus, 1000 hours | 700 - 1600 MPa | 102000 - 232000 psi | Average value: 1280 MPa Grade Count:9 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 - 1.00e+17 ohm-cm | 1.00e+14 - 1.00e+17 ohm-cm | Average value: 9.01e+15 ohm-cm Grade Count:17 |
| Surface Resistance | 1.00e+14 - 1.00e+17 ohm | 1.00e+14 - 1.00e+17 ohm | Average value: 8.01e+15 ohm Grade Count:14 |
| Dielectric Constant | 3.10 - 3.80 | 3.10 - 3.80 | Average value: 3.32 Grade Count:18 |
| Dielectric Strength | 15.7 - 30.2 kV/mm | 399 - 767 kV/in | Average value: 26.3 kV/mm Grade Count:19 |
| Dissipation Factor | 0.00100 - 0.0240 | 0.00100 - 0.0240 | Average value: 0.0106 Grade Count:15 |
| Arc Resistance | 110 - 180 sec | 110 - 180 sec | Average value: 130 sec Grade Count:4 |
| Comparative Tracking Index | 250 - 600 V | 250 - 600 V | Average value: 563 V Grade Count:14 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 40.0 - 130 µm/m-°C | 22.2 - 72.2 µin/in-°F | Average value: 99.8 µm/m-°C Grade Count:22 |
| CTE, linear, Transverse to Flow | 70.0 - 130 µm/m-°C | 38.9 - 72.2 µin/in-°F | Average value: 111 µm/m-°C Grade Count:16 |
| Melting Point | 221 - 254 °C | 430 - 489 °F | Average value: 226 °C Grade Count:20 |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 - 170 °C | 194 - 338 °F | Average value: 144 °C Grade Count:21 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 - 78.0 °C | 122 - 172 °F | Average value: 60.2 °C Grade Count:30 |
| Deflection Temperature at 8.0 MPa | 45.0 - 50.0 °C | 113 - 122 °F | Average value: 46.4 °C Grade Count:10 |
| Vicat Softening Point | 130 - 180 °C | 266 - 356 °F | Average value: 163 °C Grade Count:10 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:27 |
| Oxygen Index | 22.0 - 30.0 % | 22.0 - 30.0 % | Average value: 25.0 % Grade Count:9 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 250 - 260 °C | 482 - 500 °F | Average value: 258 °C Grade Count:15 |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | Average value: 80.0 °C Grade Count:16 |