- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 1.07
- 缺口冲击强度: 0.265
- 拉伸强度 [MPa]: 27.0
- 断裂伸长率 [%]: 48.0
- 弯曲强度 [MPa]: 8.0
- 弯曲模量 [MPa]: 0.113
- 硬度: 112.0
- 热变形温度 [℃]: 80.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 - 2.69 g/cc | 0.0387 - 0.0972 lb/in³ | Average value: 1.32 g/cc Grade Count:183 |
| Water Absorption | 0.000 - 0.600 % | 0.000 - 0.600 % | Average value: 0.283 % Grade Count:75 |
| Moisture Absorption at Equilibrium | 0.0100 - 1.09 % | 0.0100 - 1.09 % | Average value: 0.197 % Grade Count:69 |
| Water Absorption at Saturation | 0.100 - 0.500 % | 0.100 - 0.500 % | Average value: 0.418 % Grade Count:17 |
| Viscosity | 1.60 - 400000 cP | 1.60 - 400000 cP | Average value: 80000 cP Grade Count:5 |
| Viscosity Measurement | 0.665 - 1.32 | 0.665 - 1.32 | Average value: 0.964 Grade Count:15 |
| Viscosity Test | 105 - 180 cm³/g | 105 - 180 cm³/g | Average value: 133 cm³/g Grade Count:15 |
| Linear Mold Shrinkage | 0.00160 - 0.0650 cm/cm | 0.00160 - 0.0650 in/in | Average value: 0.0153 cm/cm Grade Count:137 |
| Linear Mold Shrinkage, Transverse | 0.00160 - 0.0300 cm/cm | 0.00160 - 0.0300 in/in | Average value: 0.0143 cm/cm Grade Count:55 |
| Melt Flow | 3.00 - 236 g/10 min | 3.00 - 236 g/10 min | Average value: 35.6 g/10 min Grade Count:96 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 72.0 - 90.0 | 72.0 - 90.0 | Average value: 84.0 Grade Count:23 |
| Hardness, Rockwell R | 112 - 120 | 112 - 120 | Average value: 118 Grade Count:21 |
| Hardness, Shore D | 40.0 - 87.0 | 40.0 - 87.0 | Average value: 71.3 Grade Count:26 |
| Ball Indentation Hardness | 50.0 - 160 MPa | 7250 - 23200 psi | Average value: 138 MPa Grade Count:13 |
| Tensile Strength, Ultimate | 8.00 - 165 MPa | 1160 - 23900 psi | Average value: 50.1 MPa Grade Count:89 |
| 19.0 - 32.0 MPa @Temperature 60.0 - 120 °C | 2760 - 4640 psi @Temperature 140 - 248 °F | Average value: 36.8 MPa Grade Count:1 | |
| 5.00 - 90.0 MPa @Temperature -40.0 - 160 °C | 725 - 13100 psi @Temperature -40.0 - 320 °F | Average value: 36.8 MPa Grade Count:1 | |
| 5.00 - 90.0 MPa @Strain 2.00 - 10.0 % | 725 - 13100 psi @Strain 2.00 - 10.0 % | Average value: 36.8 MPa Grade Count:1 | |
| Tensile Strength, Yield | 27.0 - 118 MPa | 3920 - 17100 psi | Average value: 53.5 MPa Grade Count:108 |
| 22.0 - 105 MPa @Temperature -40.0 - 100 °C | 3190 - 15200 psi @Temperature -40.0 - 212 °F | Average value: 63.5 MPa Grade Count:1 | |
| Elongation at Break | 1.00 - 487 % | 1.00 - 487 % | Average value: 78.1 % Grade Count:159 |
| Elongation at Yield | 2.90 - 75.0 % | 2.90 - 75.0 % | Average value: 9.86 % Grade Count:69 |
| Modulus of Elasticity | 0.115 - 21.9 GPa | 16.7 - 3180 ksi | Average value: 2.68 GPa Grade Count:92 |
| Flexural Yield Strength | 48.0 - 255 MPa | 6960 - 37000 psi | Average value: 85.4 MPa Grade Count:107 |
| 25.0 - 25.0 MPa @Temperature 90.0 - 90.0 °C | 3630 - 3630 psi @Temperature 194 - 194 °F | Average value: 25.0 MPa Grade Count:1 | |
| Flexural Modulus | 0.113 - 17.9 GPa | 16.4 - 2600 ksi | Average value: 2.54 GPa Grade Count:121 |
| 0.350 - 0.700 GPa @Temperature 60.0 - 120 °C | 50.8 - 102 ksi @Temperature 140 - 248 °F | Average value: 0.500 GPa Grade Count:2 | |
| Izod Impact, Notched | 0.265 - 8.02 J/cm | 0.496 - 15.0 ft-lb/in | Average value: 1.33 J/cm Grade Count:90 |
| 0.300 - 6.94 J/cm @Temperature -40.0 - -20.0 °C | 0.562 - 13.0 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 3.09 J/cm Grade Count:3 | |
| 1.30 - 5.70 J/cm @Temperature -40.0 - -20.0 °C | 2.44 - 10.7 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 3.09 J/cm Grade Count:5 | |
| 1.30 - 5.70 J/cm @Thickness 1.57 - 3.18 mm | 2.44 - 10.7 ft-lb/in @Thickness 0.0618 - 0.125 in | Average value: 3.09 J/cm Grade Count:5 | |
| Izod Impact, Unnotched | 2.40 - 5340 J/cm | 4.50 - 10000 ft-lb/in | Average value: 13.6 J/cm Grade Count:13 |
| Izod Impact, Notched (ISO) | 2.90 - 170 kJ/m² | 1.38 - 80.9 ft-lb/in² | Average value: 24.1 kJ/m² Grade Count:23 |
| 3.00 - 22.0 kJ/m² @Temperature -40.0 - -30.0 °C | 1.43 - 10.5 ft-lb/in² @Temperature -40.0 - -22.0 °F | Average value: 7.20 kJ/m² Grade Count:6 | |
| Izod Impact, Unnotched (ISO) | 80.0 kJ/m² - NB | 38.1 ft-lb/in² - NB | Average value: 109 kJ/m² Grade Count:6 |
| NB - NB @Temperature -30.0 - -30.0 °C | NB - NB @Temperature -22.0 - -22.0 °F | Grade Count:2 | |
| Charpy Impact Unnotched | 2.50 J/cm² - NB | 11.9 ft-lb/in² - NB | Average value: 16.2 J/cm² Grade Count:62 |
| 2.50 J/cm² - NB @Temperature -40.0 - -20.0 °C | 11.9 ft-lb/in² - NB @Temperature -40.0 - -4.00 °F | Average value: 17.2 J/cm² Grade Count:50 | |
| Charpy Impact, Notched | 0.300 - 1000 J/cm² | 1.43 - 4760 ft-lb/in² | Average value: 1.53 J/cm² Grade Count:76 |
| 0.250 - 2.50 J/cm² @Temperature -30.0 - -30.0 °C | 1.19 - 11.9 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 0.854 J/cm² Grade Count:46 | |
| Gardner Impact | 36.2 - 43.0 J | 26.7 - 31.7 ft-lb | Average value: 39.7 J Grade Count:4 |
| Tensile Impact Strength | 65.0 - 160 kJ/m² | 30.9 - 76.1 ft-lb/in² | Average value: 112 kJ/m² Grade Count:3 |
| Dart Drop, Total Energy | 100 - 140 J | 73.8 - 103 ft-lb | Average value: 130 J Grade Count:4 |
| Puncture Energy | 6.90 - 45.0 J | 5.09 - 33.2 ft-lb | Average value: 29.8 J Grade Count:8 |
| 2.00 - 32.0 J @Temperature -30.0 - -30.0 °C | 1.48 - 23.6 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 15.5 J Grade Count:6 | |
| Tensile Creep Modulus, 1 hour | 1400 - 2800 MPa | 203000 - 406000 psi | Average value: 2130 MPa Grade Count:16 |
| Tensile Creep Modulus, 1000 hours | 700 - 1800 MPa | 102000 - 261000 psi | Average value: 1260 MPa Grade Count:20 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 100 - 1.20e+17 ohm-cm | 100 - 1.20e+17 ohm-cm | Average value: 9.68e+15 ohm-cm Grade Count:109 |
| Surface Resistance | 100 - 2.00e+17 ohm | 100 - 2.00e+17 ohm | Average value: 7.76e+15 ohm Grade Count:90 |
| Dielectric Constant | 2.90 - 4.00 | 2.90 - 4.00 | Average value: 3.30 Grade Count:88 |
| Dielectric Strength | 14.0 - 140 kV/mm | 356 - 3560 kV/in | Average value: 26.4 kV/mm Grade Count:101 |
| Dissipation Factor | 0.00100 - 0.419 | 0.00100 - 0.419 | Average value: 0.0131 Grade Count:81 |
| Arc Resistance | 60.0 - 185 sec | 60.0 - 185 sec | Average value: 125 sec Grade Count:31 |
| Comparative Tracking Index | 175 - 600 V | 175 - 600 V | Average value: 538 V Grade Count:61 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 9.70 - 170 µm/m-°C | 5.39 - 94.4 µin/in-°F | Average value: 93.8 µm/m-°C Grade Count:96 |
| 124 - 139 µm/m-°C @Temperature 60.0 - 138 °C | 68.9 - 77.2 µin/in-°F @Temperature 140 - 280 °F | Average value: 132 µm/m-°C Grade Count:2 | |
| CTE, linear, Transverse to Flow | 70.0 - 170 µm/m-°C | 38.9 - 94.4 µin/in-°F | Average value: 110 µm/m-°C Grade Count:48 |
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | Average value: 1.50 J/g-°C Grade Count:4 |
| Thermal Conductivity | 0.159 - 0.270 W/m-K | 1.10 - 1.87 BTU-in/hr-ft²-°F | Average value: 0.248 W/m-K Grade Count:5 |
| Melting Point | 200 - 271 °C | 392 - 520 °F | Average value: 224 °C Grade Count:92 |
| Maximum Service Temperature, Air | 120 - 200 °C | 248 - 392 °F | Average value: 152 °C Grade Count:5 |
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 - 222 °C | 176 - 432 °F | Average value: 153 °C Grade Count:129 |
| Deflection Temperature at 1.8 MPa (264 psi) | 45.0 - 216 °C | 113 - 421 °F | Average value: 66.2 °C Grade Count:163 |
| Deflection Temperature at 8.0 MPa | 45.0 - 50.0 °C | 113 - 122 °F | Average value: 46.5 °C Grade Count:13 |
| Vicat Softening Point | 65.0 - 220 °C | 149 - 428 °F | Average value: 177 °C Grade Count:42 |
| UL RTI, Electrical | 75.0 - 130 °C | 167 - 266 °F | Average value: 113 °C Grade Count:6 |
| UL RTI, Mechanical with Impact | 75.0 - 120 °C | 167 - 248 °F | Average value: 96.0 °C Grade Count:6 |
| UL RTI, Mechanical without Impact | 75.0 - 140 °C | 167 - 284 °F | Average value: 113 °C Grade Count:6 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:143 |
| Oxygen Index | 22.0 - 32.0 % | 22.0 - 32.0 % | Average value: 24.9 % Grade Count:29 |
| Glow Wire Test | 650 - 960 °C | 1200 - 1760 °F | Average value: 829 °C Grade Count:21 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | Average value: 90.0 % Grade Count:3 |
| Gardner Color Number | 5.00 - 94.0 | 5.00 - 94.0 | Average value: 45.9 Grade Count:7 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 204 - 270 °C | 400 - 518 °F | Average value: 245 °C Grade Count:25 |
| Feed Temperature | 50.0 - 250 °C | 122 - 482 °F | Average value: 98.0 °C Grade Count:5 |
| Nozzle Temperature | 220 - 270 °C | 428 - 518 °F | Average value: 246 °C Grade Count:36 |
| Melt Temperature | 174 - 290 °C | 345 - 554 °F | Average value: 244 °C Grade Count:65 |
| Mold Temperature | 10.0 - 121 °C | 50.0 - 250 °F | Average value: 70.0 °C Grade Count:82 |
| Drying Temperature | 82.2 - 140 °C | 180 - 284 °F | Average value: 117 °C Grade Count:23 |
| Dry Time | 2.00 - 5.00 hour | 2.00 - 5.00 hour | Average value: 3.18 hour Grade Count:26 |
| Moisture Content | 0.0300 - 0.300 % | 0.0300 - 0.300 % | Average value: 0.139 % Grade Count:11 |
| Dew Point | -28.9 °C | -20.0 °F | Average value: -28.9 °C Grade Count:3 |
| Injection Pressure | 30.0 - 120 MPa | 4350 - 17400 psi | Average value: 69.5 MPa Grade Count:38 |
| Hold Pressure | 5.00 - 80.0 MPa | 725 - 11600 psi | Average value: 47.5 MPa Grade Count:26 |
| Back Pressure | 0.000 - 18.0 MPa | 0.000 - 2610 psi | Average value: 1.03 MPa Grade Count:31 |
| Screw Speed | 40.0 - 120 rpm | 40.0 - 120 rpm | Average value: 85.3 rpm Grade Count:31 |