- 熔体流动速率 [g/10min]: 4.0
- 密度 [g/cm3]: 1.25
- 吸水率 [%]: 0.05
- 缺口冲击强度: 0.22
- 拉伸强度 [MPa]: 44.0
- 断裂伸长率 [%]: 77.9
- 弯曲强度 [MPa]: 40.7
- 弯曲模量 [MPa]: 2.10
- 硬度: 117.0
- 热变形温度 [℃]: 154.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.25 - 1.73 g/cc | 0.0452 - 0.0625 lb/in³ | Average value: 1.52 g/cc Grade Count:46 |
Filler Content | 10.0 - 40.0 % | 10.0 - 40.0 % | Average value: 26.7 % Grade Count:6 |
Water Absorption | 0.0500 - 0.500 % | 0.0500 - 0.500 % | Average value: 0.147 % Grade Count:22 |
Moisture Absorption at Equilibrium | 0.0500 - 0.200 % | 0.0500 - 0.200 % | Average value: 0.139 % Grade Count:10 |
Water Absorption at Saturation | 0.450 - 0.500 % | 0.450 - 0.500 % | Average value: 0.467 % Grade Count:3 |
Viscosity Measurement | 70.0 - 120 @Temperature 240 - 300 °C | 70.0 - 120 @Temperature 464 - 572 °F | Average value: 99.5 Grade Count:2 |
Linear Mold Shrinkage | 0.00200 - 0.0400 cm/cm | 0.00200 - 0.0400 in/in | Average value: 0.0123 cm/cm Grade Count:42 |
Linear Mold Shrinkage, 6.35 mm section | 0.00300 - 0.0220 cm/cm | 0.00300 - 0.0220 in/in | Average value: 0.0134 cm/cm Grade Count:11 |
Linear Mold Shrinkage, Transverse | 0.00200 - 0.0400 cm/cm | 0.00200 - 0.0400 in/in | Average value: 0.0144 cm/cm Grade Count:15 |
Melt Flow | 4.00 - 48.0 g/10 min | 4.00 - 48.0 g/10 min | Average value: 21.0 g/10 min Grade Count:11 |
Mechanical Properties | Metric | English | Comments |
Hardness, Rockwell R | 117 - 120 | 117 - 120 | Average value: 118 Grade Count:11 |
Ball Indentation Hardness | 150 - 200 MPa | 21800 - 29000 psi | Average value: 170 MPa Grade Count:4 |
Tensile Strength, Ultimate | 40.7 - 130 MPa | 5900 - 18900 psi | Average value: 65.0 MPa Grade Count:34 |
Tensile Strength, Yield | 44.0 - 120 MPa | 6380 - 17400 psi | Average value: 55.2 MPa Grade Count:13 |
Elongation at Break | 1.80 - 16.0 % | 1.80 - 16.0 % | Average value: 3.86 % Grade Count:45 |
Elongation at Yield | 2.80 - 4.20 % | 2.80 - 4.20 % | Average value: 3.50 % Grade Count:4 |
Modulus of Elasticity | 3.10 - 15.2 GPa | 450 - 2200 ksi | Average value: 5.20 GPa Grade Count:29 |
Flexural Yield Strength | 77.9 - 207 MPa | 11300 - 30000 psi | Average value: 110 MPa Grade Count:36 |
Flexural Modulus | 2.10 - 13.1 GPa | 305 - 1900 ksi | Average value: 4.73 GPa Grade Count:39 |
Compressive Yield Strength | 49.6 - 138 MPa | 7200 - 20000 psi | Average value: 73.8 MPa Grade Count:8 |
Izod Impact, Notched | 0.220 - 12.0 J/cm | 0.412 - 22.5 ft-lb/in | Average value: 0.998 J/cm Grade Count:29 |
Izod Impact, Unnotched | 1.72 - 6.41 J/cm | 3.22 - 12.0 ft-lb/in | Average value: 3.71 J/cm Grade Count:20 |
Izod Impact, Notched (ISO) | 2.00 - 10.0 kJ/m² | 0.952 - 4.76 ft-lb/in² | Average value: 4.44 kJ/m² Grade Count:8 |
3.00 - 10.0 kJ/m² @Temperature -30.0 - -30.0 °C | 1.43 - 4.76 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 5.33 kJ/m² Grade Count:3 | |
Izod Impact, Unnotched (ISO) | 11.0 - 80.0 kJ/m² | 5.23 - 38.1 ft-lb/in² | Average value: 30.8 kJ/m² Grade Count:8 |
25.0 - 190 kJ/m² @Temperature -30.0 - -30.0 °C | 11.9 - 90.4 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 81.7 kJ/m² Grade Count:3 | |
Charpy Impact Unnotched | 2.20 - 5.00 J/cm² | 10.5 - 23.8 ft-lb/in² | Average value: 3.56 J/cm² Grade Count:11 |
1.90 - 4.50 J/cm² @Temperature -30.0 - 30.0 °C | 9.04 - 21.4 ft-lb/in² @Temperature -22.0 - 86.0 °F | Average value: 3.03 J/cm² Grade Count:10 | |
Charpy Impact, Notched | 0.170 - 1.00 J/cm² | 0.809 - 4.76 ft-lb/in² | Average value: 0.439 J/cm² Grade Count:13 |
0.200 - 1.00 J/cm² @Temperature -30.0 - 30.0 °C | 0.952 - 4.76 ft-lb/in² @Temperature -22.0 - 86.0 °F | Average value: 0.516 J/cm² Grade Count:8 | |
Tensile Creep Modulus, 1000 hours | 1300 - 2700 MPa | 189000 - 392000 psi | Average value: 2070 MPa Grade Count:3 |
Electrical Properties | Metric | English | Comments |
Electrical Resistivity | 1.00e+13 - 1.00e+18 ohm-cm | 1.00e+13 - 1.00e+18 ohm-cm | Average value: 4.12e+16 ohm-cm Grade Count:30 |
Surface Resistance | 1.00e+13 - 1.00e+17 ohm | 1.00e+13 - 1.00e+17 ohm | Average value: 1.34e+16 ohm Grade Count:16 |
Dielectric Constant | 2.60 - 4.20 | 2.60 - 4.20 | Average value: 3.72 Grade Count:17 |
Dielectric Strength | 15.0 - 100 kV/mm | 381 - 2540 kV/in | Average value: 28.3 kV/mm Grade Count:25 |
Dissipation Factor | 0.00120 - 0.130 | 0.00120 - 0.130 | Average value: 0.0202 Grade Count:14 |
Arc Resistance | 120 - 150 sec | 120 - 150 sec | Average value: 136 sec Grade Count:8 |
Comparative Tracking Index | 125 - 500 V | 125 - 500 V | Average value: 275 V Grade Count:11 |
Thermal Properties | Metric | English | Comments |
CTE, linear | 0.700 - 100 µm/m-°C | 0.389 - 55.6 µin/in-°F | Average value: 60.8 µm/m-°C Grade Count:24 |
140 - 140 µm/m-°C @Temperature 60.0 - 138 °C | 77.8 - 77.8 µin/in-°F @Temperature 140 - 280 °F | Average value: 140 µm/m-°C Grade Count:1 | |
CTE, linear, Transverse to Flow | 68.0 - 100 µm/m-°C | 37.8 - 55.6 µin/in-°F | Average value: 84.1 µm/m-°C Grade Count:11 |
150 - 150 µm/m-°C @Temperature 60.0 - 138 °C | 83.3 - 83.3 µin/in-°F @Temperature 140 - 280 °F | Average value: 150 µm/m-°C Grade Count:1 | |
Thermal Conductivity | 0.159 - 0.270 W/m-K | 1.10 - 1.87 BTU-in/hr-ft²-°F | Average value: 0.207 W/m-K Grade Count:10 |
Melting Point | 200 - 228 °C | 392 - 442 °F | Average value: 224 °C Grade Count:18 |
Deflection Temperature at 0.46 MPa (66 psi) | 154 - 220 °C | 310 - 428 °F | Average value: 192 °C Grade Count:29 |
Deflection Temperature at 1.8 MPa (264 psi) | 62.8 - 213 °C | 145 - 415 °F | Average value: 134 °C Grade Count:44 |
Vicat Softening Point | 180 - 245 °C | 356 - 473 °F | Average value: 203 °C Grade Count:10 |
Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:33 |
Oxygen Index | 21.0 - 23.0 % | 21.0 - 23.0 % | Average value: 22.3 % Grade Count:3 |
Glow Wire Test | 650 - 750 °C | 1200 - 1380 °F | Average value: 717 °C Grade Count:9 |
Processing Properties | Metric | English | Comments |
Processing Temperature | 20.0 - 271 °C | 68.0 - 520 °F | Average value: 208 °C Grade Count:17 |
Feed Temperature | 50.0 - 240 °C | 122 - 464 °F | Average value: 118 °C Grade Count:3 |
Melt Temperature | 230 - 280 °C | 446 - 536 °F | Average value: 252 °C Grade Count:15 |
Mold Temperature | 30.0 - 107 °C | 86.0 - 225 °F | Average value: 78.8 °C Grade Count:28 |
Drying Temperature | 80.0 - 130 °C | 176 - 266 °F | Average value: 119 °C Grade Count:15 |
Dry Time | 2.00 - 12.0 hour | 2.00 - 12.0 hour | Average value: 3.89 hour Grade Count:14 |
Moisture Content | 0.000 - 0.100 % | 0.000 - 0.100 % | Average value: 0.0525 % Grade Count:8 |
Injection Pressure | 50.0 - 103 MPa | 7250 - 15000 psi | Average value: 84.1 MPa Grade Count:16 |