- 密度 [g/cm3]: 1.67
- 缺口冲击强度: 0.747
- 弯曲模量 [MPa]: 10.0
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.65 g/cc | 1.65 g/cc | ASTM D792 | ||
| Density | 1.67 g/cc | 0.0603 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.16 % | 0.16 % | 23°C/50%RH; ISO 62 | ||
| Viscosity Test | 85 cm³/g | 85 cm³/g | ISO 307, 1157, 1628 | ||
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 136 MPa | 19700 psi | 5mm/min; ISO 527-2/1A | ||
| 129 MPa @Temperature 22.8 °C | 18700 psi @Temperature 73.0 °F | ASTM D638 | |||
| Elongation at Break | 2.6 % | 2.6 % | 5mm/min; ISO 527-2/1A | ||
| 2.5 % @Temperature 22.8 °C | 2.5 % @Temperature 73.0 °F | ASTM D638 | |||
| Tensile Modulus | 10.0 GPa | 1450 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 210 MPa | 30500 psi | ISO 178 | ||
| 193 MPa @Temperature 22.8 °C | 28000 psi @Temperature 73.0 °F | ASTM D790 | |||
| Flexural Modulus | 10.0 GPa | 1450 ksi | ISO 178 | ||
| 9.31 GPa @Temperature 22.8 °C | 1350 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 0.747 J/cm @Temperature 22.8 °C | 1.40 ft-lb/in @Temperature 73.0 °F | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180/1A | ||
| 8.00 kJ/m² @Temperature 30.0 °C | 3.81 ft-lb/in² @Temperature 86.0 °F | ISO 180/1A | |||
| Charpy Impact Unnotched | 5.20 J/cm² | 24.7 ft-lb/in² | ISO 179/1eU | ||
| 1.40 J/cm² @Temperature 30.0 °C | 6.66 ft-lb/in² @Temperature 86.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.790 J/cm² | 3.76 ft-lb/in² | ISO 179/1eA | ||
| 0.730 J/cm² @Temperature 30.0 °C | 3.47 ft-lb/in² @Temperature 86.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | IEC 60093 | ||
| 1.20e+17 ohm-cm | 1.20e+17 ohm-cm | ASTM D257 | |||
| Surface Resistance | >= 1.00e+17 ohm | >= 1.00e+17 ohm | IEC 60093 | ||
| Dielectric Constant | 2.8 @Frequency 100 Hz | 2.8 @Frequency 100 Hz | IEC 60250 | ||
| 3.4 @Frequency 1.00e+6 Hz | 3.4 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Dielectric Strength | 24.8 kV/mm | 630 kV/in | short term; ASTM D149 | ||
| 33.0 kV/mm | 838 kV/in | IEC 60243-1 | |||
| Dissipation Factor | 0.0070 @Frequency 1000 Hz | 0.0070 @Frequency 1000 Hz | ASTM D150 | ||
| 0.014 @Frequency 1.00e+6 Hz | 0.014 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Arc Resistance | 93 sec | 93 sec | ASTM D495 | ||
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 | ||
| 250 V | 250 V | ASTM D3638 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 75.0 µm/m-°C | 41.7 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | ASTM D648 | ||
| 210 °C | 410 °F | ISO 75-1, -2 | |||
| Vicat Softening Point | 225 °C | 437 °F | B50 (50°C/h 50N); ISO 306 | ||
| Flammability, UL94 | V-0 | V-0 | |||
| V-0 @Thickness 0.390 mm | V-0 @Thickness 0.0154 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | hopper | ||
| 65.0 - 93.0 °C | 149 - 199 °F | cavity | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 255 °C | 464 - 491 °F | |||
| Die Temperature | 250 - 255 °C | 482 - 491 °F | |||
| Melt Temperature | 235 - 255 °C | 455 - 491 °F | |||
| 260 °C | 500 °F | ISO 294 | |||
| Mold Temperature | 82.0 °C | 180 °F | ISO 294 | ||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.020 % | 0.020 % | Necessary low maximum | ||
| Injection Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Melt volume rate (MVR), cm³/10min | 13 | ||||
| MVR test load, kg | 2.16 | ||||
| MVR test temperature, °C | 250 | ||||
| Processing conditions acc. ISO | 7792-2 | ||||