- 密度 [g/cm3]: 1.2
- 缺口冲击强度: 6.41
- 拉伸强度 [MPa]: 44.1
- 弯曲模量 [MPa]: 1.60
- 热变形温度 [℃]: 106.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 | ||
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.00500 - 0.00900 cm/cm | 0.00500 - 0.00900 in/in | ASTM D955 | ||
| 0.00500 - 0.00900 cm/cm | 0.00500 - 0.00900 in/in | ISO 294-4 | |||
| Linear Mold Shrinkage, Transverse | 0.00500 - 0.00900 cm/cm | 0.00500 - 0.00900 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 44.1 MPa | 6400 psi | ASTM D638 | ||
| Tensile Stress | 35.0 MPa @Strain 50.0 % | 5080 psi @Strain 50.0 % | 50mm/min; ISO 527-2/1A | ||
| Tensile Strength, Yield | 44.1 MPa | 6400 psi | ASTM D638 | ||
| 45.0 MPa | 6530 psi | 50mm/min; ISO 527-2/1A | |||
| Elongation at Break | >= 50.0 % | >= 50.0 % | 50mm/min; ISO 527-2/1A | ||
| 185 % @Temperature 22.8 °C | 185 % @Temperature 73.0 °F | ASTM D638 | |||
| Elongation at Yield | 4.50 % | 4.50 % | 50mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 1.75 GPa | 254 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 55.0 MPa | 7980 psi | ISO 178 | ||
| 61.4 MPa | 8900 psi | ASTM D790 | |||
| Flexural Modulus | 1.60 GPa | 232 ksi | ISO 178 | ||
| 1.79 GPa @Temperature 22.8 °C | 260 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 6.41 J/cm | 12.0 ft-lb/in | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 56.0 kJ/m² | 26.6 ft-lb/in² | partial; ISO 180/1A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-2 | ||
| Transformation Temperature, Tg | 78.0 °C | 172 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ISO 75-1, -2 | ||
| 110 °C | 230 °F | ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ASTM D648 | ||
| 74.0 °C | 165 °F | ISO 75-1, -2 | |||
| Flammability, UL94 | HB | HB | UL94 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 65.0 - 96.0 °C | 149 - 205 °F | Cavity temperature | |||
| Feed Temperature | 240 - 255 °C | 464 - 491 °F | |||
| Rear Barrel Temperature | 240 - 255 °C | 464 - 491 °F | |||
| Middle Barrel Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Front Barrel Temperature | 255 - 265 °C | 491 - 509 °F | |||
| Nozzle Temperature | 260 - 270 °C | 500 - 518 °F | |||
| Zone 1 | 240 - 255 °C | 464 - 491 °F | |||
| Zone 2 | 250 - 260 °C | 482 - 500 °F | |||
| Zone 3 | 250 - 260 °C | 482 - 500 °F | |||
| Zone 4 | 255 - 265 °C | 491 - 509 °F | |||
| Die Temperature | 260 - 270 °C | 500 - 518 °F | |||
| Melt Temperature | 260 °C | 500 °F | Injection molding; ISO 294 | ||
| 260 - 280 °C | 500 - 536 °F | ||||
| 260 - 280 °C | 500 - 536 °F | ||||
| Mold Temperature | 37.8 - 121 °C | 100 - 250 °F | |||
| 82.0 °C | 180 °F | Injection molding; ISO 294 | |||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | 0.0200 % | 0.0200 % | Necessary low maximum residual | ||
| Hold Pressure | 86.0 MPa | 12500 psi | ISO 294 | ||
| Back Pressure | 0.000 - 0.689 MPa | 0.000 - 100 psi | |||
| Screw Speed | 60.0 - 125 rpm | 60.0 - 125 rpm | |||
| Hot-Working Temperature | 260 - 280 °C | 500 - 536 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Longer pre-drying times/storage | 100° C. | <= 60 h | |||
| Processing conditions | ISO 7792-2 | ||||
| Processing Notes | Medium/Fast Injection Speed | ||||