- 熔体流动速率 [g/10min]: 8.0
- 密度 [g/cm3]: 1.6
- 缺口冲击强度: 10.0
- 弯曲模量 [MPa]: 7.80
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.800 g/cc | 0.0289 lb/in³ | ISO 60 |
| Density | 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0026 cm/cm | 0.0026 in/in | 150x105x3, 260°C / MT 80°C; 500 bar; ISO 2577 |
| Linear Mold Shrinkage, Transverse | 0.0104 cm/cm | 0.0104 in/in | 150x105x3, 260°C / MT 80°C; 500 bar; ISO 2577 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 260 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 500 °F | ISO 1133-1 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 120 MPa | 17400 psi | 5 mm/min; ISO 527-1,-2 |
| Elongation at Break | 3.1 % | 3.1 % | 5 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 9.00 GPa | 1310 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 195 MPa | 28300 psi | 2 mm/min; ISO 178-A |
| Flexural Modulus | 7.80 GPa | 1130 ksi | 2 mm/min; ISO 178-A |
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² @Temperature -30.0 °C | <= 4.76 ft-lb/in² @Temperature -22.0 °F | ISO 180-1A |
| <= 10.0 kJ/m² @Temperature -40.0 °C | <= 4.76 ft-lb/in² @Temperature -40.0 °F | ISO 180-1A | |
| 10.0 kJ/m² @Temperature 23.0 °C | 4.76 ft-lb/in² @Temperature 73.4 °F | ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 55.0 kJ/m² @Temperature 23.0 °C | 26.2 ft-lb/in² @Temperature 73.4 °F | ISO 180-1U |
| Charpy Impact Unnotched | 7.00 J/cm² @Temperature 23.0 °C | 33.3 ft-lb/in² @Temperature 73.4 °F | ISO 179-1eU |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C | <= 4.76 ft-lb/in² @Temperature -22.0 °F | ISO 179-1eA |
| 1.20 J/cm² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | ISO 179-1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 60093 |
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz | 3.7 @Frequency 1.00e+6 Hz | IEC 60250 |
| 3.8 @Frequency 100 Hz | 3.8 @Frequency 100 Hz | IEC 60250 | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 |
| Comparative Tracking Index | 225 V | 225 V | Solution A; UL 746A |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 16.7 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 50.0 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1,-2 |
| Melting Point | 225 °C | 437 °F | 10 °C/min; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1,-2 |
| Deflection Temperature at 8.0 MPa | 110 °C | 230 °F | ISO 75-1,-2 |
| Vicat Softening Point | 200 °C | 392 °F | 50 N; 50 °C/h; ISO 306 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |
| V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | ||
| Oxygen Index | 32 % | 32 % | Method A; ISO 4589-2 |
| Shrinkage | 0.070 % | 0.070 % | post-shrinkage, transverse, 150x105x3, 120°C; 4 h; ISO 2577 |
| 0.26 % | 0.26 % | post-shrinkage, 150x105x3, 120°C; 4 h; ISO 2577 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 °C | 500 °F | Injection molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection molding; ISO 294 |
| Dry Time | 4.00 - 8.00 hour @Temperature 120 °C | 4.00 - 8.00 hour @Temperature 248 °F | |
| Moisture Content | 0.00 - 0.020 % | 0.00 - 0.020 % | Karl Fischer test |