- 熔体流动速率 [g/10min]: 10.0
- 密度 [g/cm3]: 1.29
- 缺口冲击强度: 7.5
- 拉伸强度 [MPa]: 53.0
- 弯曲模量 [MPa]: 2.27
- 硬度: 110.0
- 热变形温度 [℃]: 109.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0095 cm/cm | 0.0060 - 0.0095 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min @Load 5.00 kg, Temperature 260 °C | 10 g/10 min @Load 11.0 lb, Temperature 500 °F | ASTM D1238 |
| 13 g/10 min @Load 5.00 kg, Temperature 265 °C | 13 g/10 min @Load 11.0 lb, Temperature 509 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 110 @Thickness 3.20 mm | 110 @Thickness 0.126 in | Injection Molded; ASTM D785 |
| Tensile Strength at Break | 45.0 MPa @Thickness 3.20 mm | 6530 psi @Thickness 0.126 in | 50 mm/min, Injection Molded; ASTM D638 |
| Tensile Strength, Yield | 53.0 MPa @Thickness 3.20 mm | 7690 psi @Thickness 0.126 in | 50 mm/min, Injection Molded; ASTM D638 |
| Elongation at Break | 150 % @Thickness 3.20 mm | 150 % @Thickness 0.126 in | 50 mm/min, Injection Molded; ASTM D638 |
| Elongation at Yield | 4.1 % @Thickness 3.20 mm | 4.1 % @Thickness 0.126 in | 50 mm/min, Injection Molded; ASTM D638 |
| Tensile Modulus | 2.33 GPa @Thickness 3.20 mm | 338 ksi @Thickness 0.126 in | 5 mm/min, Injection Molded; ASTM D638 |
| Flexural Strength | 82.0 MPa @Thickness 3.20 mm | 11900 psi @Thickness 0.126 in | 1.3 mm/min, Injection Molded; ASTM D790 |
| Flexural Modulus | 2.27 GPa @Thickness 3.20 mm | 329 ksi @Thickness 0.126 in | 1.3 mm/min, Injection Molded; ASTM D790 |
| Izod Impact, Notched | 7.50 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | 14.1 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | Injection Molded; ASTM D256 |
| Dart Drop, Total Energy | 45.0 J @Thickness 3.20 mm, Temperature 23.0 °C | 33.2 ft-lb @Thickness 0.126 in, Temperature 73.4 °F | Injection Molded, Peak Energy; ASTM D3763 |
| 49.0 J @Thickness 3.20 mm, Temperature 0.000 °C | 36.1 ft-lb @Thickness 0.126 in, Temperature 32.0 °F | Injection Molded, Peak Energy; ASTM D3763 | |
| 60.0 J @Thickness 3.20 mm, Temperature 23.0 °C | 44.3 ft-lb @Thickness 0.126 in, Temperature 73.4 °F | Injection Molded, Total Energy; ASTM D3763 | |
| 62.0 J @Thickness 3.20 mm, Temperature 0.000 °C | 45.7 ft-lb @Thickness 0.126 in, Temperature 32.0 °F | Injection Molded, Total Energy; ASTM D3763 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 74.0 µm/m-°C @Temperature -40.0 - 80.0 °C | 41.1 µin/in-°F @Temperature -40.0 - 176 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 79.0 °C | 174 °F | Unannealed; ASTM D648 |
| Vicat Softening Point | 140 °C @Load 1.02 kg | 284 °F @Load 2.25 lb | Rate B (120°C/h); ASTM D1525 |
| Flammability, UL94 | 2.00 @Thickness 1.50 mm | 2.00 @Thickness 0.0591 in | |
| V-0 @Thickness 2.00 mm | V-0 @Thickness 0.0787 in | ||
| 5VB @Thickness 2.50 mm | 5VB @Thickness 0.0984 in | ||
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 249 - 282 °C | 480 - 540 °F | |
| Mold Temperature | 43.3 - 65.6 °C | 110 - 150 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | |