- 熔体流动速率 [g/10min]: 10.0
- 密度 [g/cm3]: 1.35
- 吸水率 [%]: 0.42
- 缺口冲击强度: 0.6
- 拉伸强度 [MPa]: 55.0
- 断裂伸长率 [%]: 90.0
- 弯曲模量 [MPa]: 4.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D 792 |
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.14 % | 0.14 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.42 % @Temperature 23.0 °C | 0.42 % @Temperature 73.4 °F | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0060 in/in @Thickness 0.126 in | SABIC Method |
| Melt Flow | 10 g/10 min @Load 5.00 kg, Temperature 265 °C | 10 g/10 min @Load 11.0 lb, Temperature 509 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 11 g/10 min @Load 5.00 kg, Temperature 266 °C | 11 g/10 min @Load 11.0 lb, Temperature 511 °F | ASTM D 1238 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | Type I, 5 mm/min; ASTM D 638 |
| 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | Type I, 5 mm/min; ASTM D 638 |
| 56.0 MPa | 8120 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 8.0 % | 8.0 % | 5 mm/min; ISO 527 |
| 10 % | 10 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 3.2 % | 3.2 % | Type I, 5 mm/min; ASTM D 638 |
| 3.2 % | 3.2 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 4.30 GPa | 624 ksi | 1 mm/min; ISO 527 |
| 4.40 GPa | 638 ksi | 5 mm/min; ASTM D 638 | |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 4.20 GPa | 609 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 4.20 GPa | 609 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.600 J/cm @Temperature -30.0 °C | 1.12 ft-lb/in @Temperature -22.0 °F | ASTM D 256 |
| 0.800 J/cm @Temperature 23.0 °C | 1.50 ft-lb/in @Temperature 73.4 °F | ASTM D 256 | |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1A |
| 8.00 kJ/m² @Temperature 23.0 °C | 3.81 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 80.0 kJ/m² @Temperature -30.0 °C | 38.1 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1U |
| 100 kJ/m² @Temperature 23.0 °C | 47.6 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1U | |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature 23.0 °C | 2.86 ft-lb/in² @Temperature 73.4 °F | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Impact Test | 45.0 J @Temperature 23.0 °C | 33.2 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 43.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 23.9 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 48.0 µm/m-°C @Temperature -30.0 - 80.0 °C | 26.7 µin/in-°F @Temperature -22.0 - 176 °F | ISO 11359-2 | |
| 48.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 26.7 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 64.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 35.6 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 68.0 µm/m-°C @Temperature -30.0 - 80.0 °C | 37.8 µin/in-°F @Temperature -22.0 - 176 °F | ISO 11359-2 | |
| 68.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 37.8 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 112 °C | 234 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 112 °C @Thickness 3.20 mm | 234 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| Vicat Softening Point | 138 °C | 280 °F | Rate B/50; ASTM D 1525 |
| 138 °C | 280 °F | Rate B/50; ISO 306 | |
| 140 °C | 284 °F | Rate B/120; ISO 306 | |