- 熔体流动速率 [g/10min]: 38.0
- 密度 [g/cm3]: 1.46
- 吸水率 [%]: 0.36
- 缺口冲击强度: 0.5
- 拉伸强度 [MPa]: 95.0
- 断裂伸长率 [%]: 145
- 弯曲模量 [MPa]: 5.30
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.13 % | 0.13 % | 23°C / 50% RH; ISO 62 | ||
| Water Absorption at Saturation | 0.36 % @Temperature 23.0 °C | 0.36 % @Temperature 73.4 °F | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0032 - 0.0040 cm/cm | 0.0032 - 0.0040 in/in | on tensile bar; SABIC Method | ||
| Melt Flow | 38 g/10 min @Load 5.00 kg, Temperature 265 °C | 38 g/10 min @Load 11.0 lb, Temperature 509 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 95.0 MPa | 13800 psi | ASTM D 638 | ||
| 105 MPa | 15200 psi | 5 mm/min; ISO 527 | |||
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | ASTM D 638 | ||
| 105 MPa | 15200 psi | 5 mm/min; ISO 527 | |||
| Elongation at Break | 1.8 % | 1.8 % | ASTM D 638 | ||
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |||
| Elongation at Yield | 1.8 % | 1.8 % | ASTM D 638 | ||
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |||
| Tensile Modulus | 6.25 GPa | 906 ksi | 5 mm/min; ASTM D 638 | ||
| 6.40 GPa | 928 ksi | 1 mm/min; ISO 527 | |||
| Flexural Yield Strength | 145 MPa | 21000 psi | 2 mm/min; ISO 178 | ||
| Flexural Modulus | 5.30 GPa | 769 ksi | 2 mm/min; ISO 178 | ||
| Izod Impact, Notched | 0.500 J/cm @Temperature 23.0 °C | 0.937 ft-lb/in @Temperature 73.4 °F | ASTM D 256 | ||
| 0.500 J/cm @Temperature -30.0 °C | 0.937 ft-lb/in @Temperature -22.0 °F | ASTM D 256 | |||
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C | 2.86 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1A | ||
| 6.00 kJ/m² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 19.0 kJ/m² @Temperature 23.0 °C | 9.04 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1U | ||
| 19.0 kJ/m² @Temperature -30.0 °C | 9.04 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1U | |||
| Charpy Impact, Notched | 0.600 J/cm² @Temperature 23.0 °C | 2.86 ft-lb/in² @Temperature 73.4 °F | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 31.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 17.2 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 94.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 52.2 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af | ||
| Vicat Softening Point | 230 °C | 446 °F | Rate B/50; ISO 306 | ||
| 230 °C | 446 °F | Rate B/120; ISO 306 | |||
| Descriptive Properties | |||||
| Ball Pressure Test, 125°C +/- 2°C | PASS | IEC 60695-10-2 | |||