- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 1.2
- 吸水率 [%]: 0.28
- 缺口冲击强度: 0.8
- 拉伸强度 [MPa]: 60.0
- 断裂伸长率 [%]: 93.0
- 弯曲模量 [MPa]: 2.18
- 热变形温度 [℃]: 122.0
- 透光率 [%]: 79.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.070 % | 0.070 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.28 % @Temperature 23.0 °C | 0.28 % @Temperature 73.4 °F | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0060 - 0.0080 in/in @Thickness 0.126 in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0060 - 0.0080 in/in @Thickness 0.126 in | SABIC Method |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 265 °C | 3.0 g/10 min @Load 4.76 lb, Temperature 509 °F | ASTM D 1238 |
| 15 g/10 min @Load 10.0 kg, Temperature 265 °C | 15 g/10 min @Load 22.0 lb, Temperature 509 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D 638 |
| 65.0 MPa | 9430 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
| 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Break | 110 % | 110 % | Type I, 50 mm/min; ASTM D 638 |
| 135 % | 135 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 6.0 % | 6.0 % | Type I, 50 mm/min; ASTM D 638 |
| 6.0 % | 6.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.30 GPa | 334 ksi | 50 mm/min; ASTM D 638 |
| 2.40 GPa | 348 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 93.0 MPa | 13500 psi | 2 mm/min; ISO 178 |
| 95.0 MPa | 13800 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 2.18 GPa | 316 ksi | 2 mm/min; ISO 178 |
| 2.28 GPa | 331 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.800 J/cm @Temperature -30.0 °C | 1.50 ft-lb/in @Temperature -22.0 °F | ASTM D 256 |
| 10.0 J/cm @Temperature 23.0 °C | 18.7 ft-lb/in @Temperature 73.4 °F | ASTM D 256 | |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1A |
| 15.0 kJ/m² @Temperature 23.0 °C | 7.14 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1A | |
| 78.0 kJ/m² @Temperature 23.0 °C | 37.1 ft-lb/in² @Temperature 73.4 °F | 63.5*12.7*3.2; ISO 180/4A | |
| Charpy Impact, Notched | 2.20 J/cm² @Temperature 23.0 °C | 10.5 ft-lb/in² @Temperature 73.4 °F | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Impact Test | 85.0 J @Temperature 23.0 °C | 62.7 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature -40.0 - 95.0 °C | 38.9 µin/in-°F @Temperature -40.0 - 203 °F | ASTM E 831 |
| 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 38.9 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature -40.0 - 95.0 °C | 38.9 µin/in-°F @Temperature -40.0 - 203 °F | ASTM E 831 |
| 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 38.9 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| 122 °C @Thickness 3.20 mm | 252 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 111 °C | 232 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 111 °C @Thickness 3.20 mm | 232 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| Vicat Softening Point | 127 °C | 261 °F | Rate B/50; ISO 306 |
| 129 °C | 264 °F | Rate B/120; ISO 306 | |
| 130 °C | 266 °F | Rate B/50; ASTM D 1525 | |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 79 % @Thickness 2.54 mm | 79 % @Thickness 0.100 in | ASTM D 1003 |