- 密度 [g/cm3]: 1.35
- 缺口冲击强度: 1.87
- 断裂伸长率 [%]: 144.8
- 弯曲模量 [MPa]: 5.41
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 - 0.0060 cm/cm | 0.0010 - 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 89.6 MPa | 13000 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Yield Strength | 144.8 MPa | 21000 psi | ASTM D790 |
| Flexural Modulus | 5.41 GPa | 785 ksi | ASTM D790 |
| Izod Impact, Notched | 1.87 J/cm | 3.50 ft-lb/in | 1/8" sample; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 116 °C | 241 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 - 282 °C | 500 - 540 °F | Injection |
| Mold Temperature | 77.0 - 116 °C | 171 - 241 °F | |