- 密度 [g/cm3]: 1.25
- 缺口冲击强度: 8.01
- 拉伸强度 [MPa]: 61.7
- 断裂伸长率 [%]: 82.7
- 弯曲模量 [MPa]: 2.29
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 60.3 MPa | 8750 psi | ASTM D638 |
| Tensile Strength, Yield | 61.7 MPa | 8950 psi | ASTM D638 |
| Flexural Yield Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 2.29 GPa | 332 ksi | ASTM D790 |
| Izod Impact, Notched | 8.01 J/cm | 15.0 ft-lb/in | 1/8" sample; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 277 - 288 °C | 531 - 550 °F | Injection |
| Mold Temperature | 54.0 - 71.0 °C | 129 - 160 °F | |