- 熔体流动速率 [g/10min]: 19.1
- 密度 [g/cm3]: 1.3
- 缺口冲击强度: 6.9
- 拉伸强度 [MPa]: 62.1
- 弯曲模量 [MPa]: 2.63
- 热变形温度 [℃]: 255.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| Melt Flow | 19.1 g/10 min @Load 5.00 kg, Temperature 265 °C | 19.1 g/10 min @Load 11.0 lb, Temperature 509 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 62.1 MPa | 9010 psi | ASTM D638 |
| Elongation at Break | 130 % | 130 % | ASTM D638 |
| Flexural Modulus | 2.63 GPa | 381 ksi | ASTM D790 |
| Izod Impact, Notched | 6.90 J/cm | 12.9 ft-lb/in | ASTM D256 |
| 4.30 J/cm @Temperature -40.0 °C | 8.06 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 222 °C | 432 °F | ASTM D648 |
| Flammability, UL94 | V-2 | V-2 | Pending |