- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D1505 | ||
| Thickness | 37.5 microns | 1.48 mil | 2:1 blow-up ratio | ||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 9.00 MPa | 1310 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 9.80 MPa | 1420 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 580 % | 580 % | ASTM D-882 | ||
| Film Elongation at Break, TD | 800 % | 800 % | ASTM D-882 | ||
| Secant Modulus, MD | 0.200 GPa | 29.0 ksi | value @ 0.1 mm/mm-min Initial strain rate; ASTM D-882 | ||
| Secant Modulus, TD | 0.241 GPa | 35.0 ksi | value @ 0.1 mm/mm-min Initial strain rate; ASTM D-882 | ||
| Elmendorf Tear Strength, MD | 6.70 g/micron | 170 g/mil | ASTM D-1922 | ||
| Elmendorf Tear Strength, TD | 16.6 g/micron | 422 g/mil | ASTM D-1922 | ||
| Film Tensile Strength at Break, MD | 26.9 MPa | 3900 psi | ASTM D-882 | ||
| Film Tensile Strength at Break, TD | 20.7 MPa | 3000 psi | ASTM D-882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 20 % | 20 % | ASTM D-1003 | ||
| Gloss | 38 % | 38 % | ASTM D-2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 199 - 227 °C | 390 - 441 °F | |||
| Descriptive Properties | |||||
| process | Film | ||||
| region | Europe/Turkey | ||||
| International | |||||
| Mexico | |||||
| US & Canada | |||||