- 熔体流动速率 [g/10min]: 0.57
- 密度 [g/cm3]: 0.916
- 脆化温度 [℃]: -90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.916 - 0.938 g/cc | 0.0331 - 0.0339 lb/in³ | Average value: 0.920 g/cc Grade Count:84 |
| Thickness | 10.0 - 50.0 microns | 0.394 - 1.97 mil | Average value: 32.1 microns Grade Count:41 |
| Melt Flow | 0.570 - 4.10 g/10 min | 0.570 - 4.10 g/10 min | Average value: 1.34 g/10 min Grade Count:84 |
| Antiblock Level | 0.000 - 3200 ppm | 0.000 - 3200 ppm | Average value: 1350 ppm Grade Count:6 |
| Slip Level | 0.000 - 1500 ppm | 0.000 - 1500 ppm | Average value: 725 ppm Grade Count:6 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.00 - 17.0 MPa | 1310 - 2470 psi | Average value: 11.1 MPa Grade Count:48 |
| Film Tensile Strength at Yield, TD | 8.00 - 18.0 MPa | 1160 - 2610 psi | Average value: 10.9 MPa Grade Count:48 |
| Film Elongation at Break, MD | 498 - 1220 % | 498 - 1220 % | Average value: 700 % Grade Count:80 |
| Film Elongation at Break, TD | 675 - 1440 % | 675 - 1440 % | Average value: 861 % Grade Count:80 |
| Film Elongation at Yield, MD | 19.0 - 47.0 % | 19.0 - 47.0 % | Average value: 28.4 % Grade Count:5 |
| Film Elongation at Yield, TD | 12.0 - 35.0 % | 12.0 - 35.0 % | Average value: 18.0 % Grade Count:5 |
| Secant Modulus, MD | 0.0900 - 0.390 GPa | 13.1 - 56.6 ksi | Average value: 0.196 GPa Grade Count:63 |
| Secant Modulus, TD | 0.100 - 0.450 GPa | 14.5 - 65.3 ksi | Average value: 0.224 GPa Grade Count:63 |
| Coefficient of Friction | 0.100 - 1.00 | 0.100 - 1.00 | Average value: 0.414 Grade Count:50 |
| Elmendorf Tear Strength MD | 20.0 - 160 g | 20.0 - 160 g | Average value: 102 g Grade Count:20 |
| Elmendorf Tear Strength TD | 180 - 520 g | 180 - 520 g | Average value: 356 g Grade Count:20 |
| Elmendorf Tear Strength, MD | 0.530 - 7.10 g/micron | 13.5 - 180 g/mil | Average value: 3.98 g/micron Grade Count:71 |
| Elmendorf Tear Strength, TD | 2.04 - 25.6 g/micron | 51.8 - 650 g/mil | Average value: 15.2 g/micron Grade Count:71 |
| Dart Drop | 1.58 - 5.31 g/micron | 40.1 - 135 g/mil | Average value: 3.22 g/micron Grade Count:51 |
| Dart drop Test | 45.0 - 250 g | 0.0992 - 0.551 lb | Average value: 118 g Grade Count:41 |
| Film Tensile Strength at Break, MD | 25.0 - 52.0 MPa | 3630 - 7540 psi | Average value: 36.8 MPa Grade Count:80 |
| Film Tensile Strength at Break, TD | 18.6 - 47.0 MPa | 2700 - 6820 psi | Average value: 29.5 MPa Grade Count:80 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 120 - 127 °C | 248 - 261 °F | Average value: 122 °C Grade Count:18 |
| Vicat Softening Point | 84.0 - 118 °C | 183 - 244 °F | Average value: 99.9 °C Grade Count:29 |
| Brittleness Temperature | -90.0 - -60.0 °C | -130 - -76.0 °F | Average value: -68.9 °C Grade Count:21 |
| Antiblock | 1700 - 7500 | 1700 - 7500 | Average value: 5400 Grade Count:3 |
| Optical Properties | Metric | English | Comments |
| Haze | 1.30 - 61.0 % | 1.30 - 61.0 % | Average value: 15.0 % Grade Count:80 |
| Gloss | 19.0 - 140 % | 19.0 - 140 % | Average value: 62.1 % Grade Count:80 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 170 - 220 °C | 338 - 428 °F | Average value: 194 °C Grade Count:5 |
| Melt Temperature | 123 - 260 °C | 253 - 500 °F | Average value: 209 °C Grade Count:40 |
| Mold Temperature | 225 °C | 437 °F | Average value: 225 °C Grade Count:4 |
| Die Opening | 0.0900 - 0.250 cm | 0.0354 - 0.0984 in | Average value: 0.181 cm Grade Count:7 |
| Blow-up Ratio (BUR) | 2.00 - 3.00 | 2.00 - 3.00 | Average value: 2.50 Grade Count:11 |