- 熔体流动速率 [g/10min]: 1.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 0.916 g/cc | 0.916 g/cc | ASTM D1505/D792 |
Thickness | 25.0 microns | 0.984 mil | |
Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
Film Elongation at Break, MD | 1130 % | 1130 % | ASTM D882 |
Film Elongation at Break, TD | 1430 % | 1430 % | ASTM D882 |
Elmendorf Tear Strength TD | 370 g | 370 g | gF; ASTM D1922 |
Dart drop Test | 120 g | 0.265 lb | g/F50; ASTM D1709 |
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM D882 |
Film Tensile Strength at Break, TD | 40.0 MPa | 5800 psi | ASTM D882 |
1% Secant Modulus, MD | 180 MPa | 26100 psi | ASTM D882 |
1% Secant Modulus, TD | 200 MPa | 29000 psi | ASTM D882 |
Optical Properties | Metric | English | Comments |
Haze | 37 % | 37 % | ASTM D1003 |
Gloss | 48 % | 48 % | 60°; ASTM D2457 |