- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.916
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.916 g/cc | 0.0331 lb/in³ | ASTM D1505 | ||
| Thickness | 38.0 microns | 1.50 mil | |||
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 1347 % | 1347 % | ASTM D882 | ||
| Film Elongation at Break, TD | 1639 % | 1639 % | ASTM D882 | ||
| Secant Modulus, MD | 0.171 GPa | 24.8 ksi | 1%; ASTM D882 | ||
| Secant Modulus, TD | 0.171 GPa | 24.8 ksi | 1%; ASTM D882 | ||
| Coefficient of Friction | >= 1.0 | >= 1.0 | ASTM D1894 | ||
| Elmendorf Tear Strength, MD | 10.0 g/micron | 254 g/mil | ASTM 1922 | ||
| Elmendorf Tear Strength, TD | 18.7 g/micron | 475 g/mil | ASTM 1922 | ||
| Dart Drop | 3.31 g/micron | 84.1 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 52.0 MPa | 7540 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 41.0 MPa | 5950 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 21.9 % | 21.9 % | ASTM D1003 | ||
| Gloss | 6.8 % | 6.8 % | 60° angle; ASTM D2457 | ||
| Descriptive Properties | |||||
| Minimum Recommended Thickness | 15 µm | ||||