- 熔体流动速率 [g/10min]: 2.3
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 0.918 g/cc | 0.918 g/cc | ASTM D1505/D792 |
Thickness | 25.0 microns | 0.984 mil | |
Melt Flow | 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.3 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
Film Elongation at Break, MD | 1310 % | 1310 % | ASTM D882 |
Film Elongation at Break, TD | 1560 % | 1560 % | ASTM D882 |
Elmendorf Tear Strength MD | 150 g | 150 g | gF; ASTM D1922 |
Elmendorf Tear Strength TD | 190 g | 190 g | gF; ASTM D1922 |
Dart drop Test | 100 g | 0.221 lb | g/F50; ASTM D1709 |
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
1% Secant Modulus, MD | 200 MPa | 29000 psi | ASTM D882 |
1% Secant Modulus, TD | 230 MPa | 33400 psi | ASTM D882 |
Optical Properties | Metric | English | Comments |
Haze | 54 % | 54 % | ASTM D1003 |
Gloss | 24 % | 24 % | 60°; ASTM D2457 |