- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D1505 | ||
| Thickness | 38.0 microns | 1.50 mil | |||
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 1114 % | 1114 % | ASTM D882 | ||
| Film Elongation at Break, TD | 1422 % | 1422 % | ASTM D882 | ||
| Secant Modulus, MD | 0.165 GPa | 23.9 ksi | 1%; ASTM D882 | ||
| Secant Modulus, TD | 0.190 GPa | 27.6 ksi | 1%; ASTM D882 | ||
| Coefficient of Friction | 0.19 | 0.19 | ASTM D1894 | ||
| Elmendorf Tear Strength, MD | 4.60 g/micron | 117 g/mil | ASTM 1922 | ||
| Elmendorf Tear Strength, TD | 21.5 g/micron | 546 g/mil | ASTM 1922 | ||
| Dart Drop | 2.89 g/micron | 73.4 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 44.0 MPa | 6380 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 8.7 % | 8.7 % | ASTM D1003 | ||
| Gloss | 10.9 % | 10.9 % | 60° angle; ASTM D2457 | ||
| Descriptive Properties | |||||
| Additives | Antiblock, Slip, LLDPE and PPA | ||||
| Minimum Recommended Thickness | 30 µm | ||||