- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ASTM-D792 |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 930 % | 930 % | ASTM-D882 |
| Film Elongation at Break, TD | 1280 % | 1280 % | ASTM-D882 |
| Elmendorf Tear Strength MD | 120 g | 120 g | ASTM-D1922 |
| Elmendorf Tear Strength TD | 400 g | 400 g | ASTM-D1922 |
| Elmendorf Tear Strength, MD | 4.80 g/micron | 122 g/mil | ASTM-D1922 |
| Elmendorf Tear Strength, TD | 16.0 g/micron | 406 g/mil | ASTM-D1922 |
| Dart Drop | 3.20 g/micron | 81.3 g/mil | ASTM-D1709 |
| Dart drop Test | 80.0 g | 0.176 lb | ASTM-D1709 |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM-D882 |
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM-D882 |
| 1% Secant Modulus, MD | 160 MPa | 23200 psi | ASTM-D882 |
| 1% Secant Modulus, TD | 180 MPa | 26100 psi | ASTM-D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 11 % | 11 % | ASTM-D1003 |
| Gloss | 107 % | 107 % | Angle 60°; ASTM-D2457 |