- 熔体流动速率 [g/10min]: 0.75
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM-D792 |
| Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.75 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 940 % | 940 % | ASTM-D882 |
| Film Elongation at Break, TD | 1260 % | 1260 % | ASTM-D882 |
| Elmendorf Tear Strength MD | 350 g | 350 g | ASTM-D1922 |
| Elmendorf Tear Strength TD | 780 g | 780 g | ASTM-D1922 |
| Elmendorf Tear Strength, MD | 14.0 g/micron | 356 g/mil | ASTM-D1922 |
| Elmendorf Tear Strength, TD | 31.2 g/micron | 792 g/mil | ASTM-D1922 |
| Dart Drop | 9.20 g/micron | 234 g/mil | ASTM-D1709 |
| Dart drop Test | 230 g | 0.507 lb | ASTM-D1709 |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM-D882 |
| Film Tensile Strength at Break, TD | 40.0 MPa | 5800 psi | ASTM-D882 |
| 1% Secant Modulus, MD | 150 MPa | 21800 psi | ASTM-D882 |
| 1% Secant Modulus, TD | 180 MPa | 26100 psi | ASTM-D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 9.0 % | 9.0 % | ASTM-D1003 |
| Gloss | 113 % | 113 % | Angle 60°; ASTM-D2457 |