- 密度 [g/cm3]: 0.929
- 拉伸强度 [MPa]: 11.0
- 弯曲模量 [MPa]: 0.524
- 热变形温度 [℃]: 47.2
- 脆化温度 [℃]: -30.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.929 g/cc | 0.0336 lb/in³ | ASTM D792 |
| ESCR 100% Igepal® | <= 1.0 hour @Temperature 50.0 °C | <= 1.0 hour @Temperature 122 °F | F50; Molded and tested in accordance with ASTM D4976; ASTM D1693 |
| Melt Index of Compound | 100 g/10 min @Load 2.16 kg, Temperature 190 °C | 100 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 53 | 53 | Molded and tested in accordance with ASTM D4976; ASTM D2240 |
| Tensile Strength at Break | 8.27 MPa | 1200 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Break | 120 % | 120 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Yield | 2.0 % | 2.0 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Flexural Modulus | 0.524 GPa | 76.0 ksi | 2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 B |
| Tensile Impact Strength | 168 kJ/m² | 80.0 ft-lb/in² | Molded and tested in accordance with ASTM D4976; ASTM D1822, Type S |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126 °C | 259 °F | Dow Method (DSC) |
| Crystallization Temperature | 112 °C | 234 °F | Dow Method (DSC) |
| Deflection Temperature at 0.46 MPa (66 psi) | 47.2 °C | 117 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
| Vicat Softening Point | 96.1 °C | 205 °F | ASTM D1525 |
| Brittleness Temperature | -30.0 °C | -22.0 °F | Molded and tested in accordance with ASTM D4976; ASTM D746 |