- 熔体流动速率 [g/10min]: 4.0
- 密度 [g/cm3]: 0.941
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.941 g/cc | 0.0340 lb/in³ | ASTM D792 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 16.22 MPa | 2352 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.76 MPa | 1561 psi | ASTM D882 |
| Film Elongation at Break, MD | 575 % | 575 % | ASTM D882 |
| Film Elongation at Break, TD | 740 % | 740 % | ASTM D882 |
| Impact | 1365 | 1365 | [ft-lbf/in3]; Toughness MD; ASTM D882 |
| 1498 | 1498 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 34 g | 34 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 209 g | 209 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 1.34 g/micron | 34.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 8.23 g/micron | 209 g/mil | ASTM D1922 |
| Dart drop Test | 43.0 g | 0.0948 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 39.03 MPa | 5661 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 27.98 MPa | 4058 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 127 °C | 261 °F | Dow Method (DSC) |
| Vicat Softening Point | 123 °C | 253 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 4.1 % | 4.1 % | ASTM D1003 |
| Gloss | 86 % | 86 % | 45°; ASTM D2457 |