- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.925
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ASTM D792 |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.70 MPa | 1697 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.42 MPa | 1511 psi | ASTM D882 |
| Film Elongation at Break, MD | 418 % | 418 % | ASTM D882 |
| Film Elongation at Break, TD | 798 % | 798 % | ASTM D882 |
| Impact | 262 | 262 | [ft-lbf/in3]; Puncture Resistance; Dow Method |
| 1070 | 1070 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| 1714 | 1714 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 158 g | 158 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 576 g | 576 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 7.776 g/micron | 197.5 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 28.3 g/micron | 720 g/mil | ASTM D1922 |
| Dart drop Test | 94.0 g | 0.207 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 50.21 MPa | 7282 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 40.48 MPa | 5871 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 124 °C | 255 °F | Dow Method (DSC) |
| Vicat Softening Point | 108 °C | 226 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 1.2 % | 1.2 % | ASTM D1003 |
| Gloss | 93.4 % | 93.4 % | 45°; ASTM D2457 |