- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.916
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.916 g/cc | 0.0331 lb/in³ | ASTM D792 |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.818 MPa | 1424 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.17 MPa | 1475 psi | ASTM D882 |
| Film Elongation at Break, MD | 609 % | 609 % | ASTM D882 |
| Film Elongation at Break, TD | 671 % | 671 % | ASTM D882 |
| Secant Modulus, MD | 0.165846 GPa | 24.0544 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.191212 GPa | 27.7334 ksi | 2% Secant; ASTM D882 |
| Impact | 27 | 27 | [lbf]; Puncture Resistance Force; Dow Method |
| 334 | 334 | [ft-lbf/in3]; Puncture Resistance; Dow Method | |
| Puncture Energy | 11.9 J | 8.75 ft-lb | Dow Method |
| Elmendorf Tear Strength MD | 825 g | 825 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 1014 g | 1014 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 16.24 g/micron | 412.5 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 20.0 g/micron | 507 g/mil | ASTM D1922 |
| Dart drop Test | >= 850 g | >= 1.87 lb | Method B; ASTM D1709 |
| Film Tensile Strength at Break, MD | 56.85 MPa | 8246 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 52.84 MPa | 7664 psi | ASTM D882 |
| Heat Seal Strength Initiation Temperature | 99.0 °C | 210 °F | 2 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 123 °C | 253 °F | Dow Method (DSC) |
| Vicat Softening Point | 101 °C | 214 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 9.0 % | 9.0 % | ASTM D1003 |
| Gloss | 70 % | 70 % | 45°; ASTM D2457 |