- 熔体流动速率 [g/10min]: 3.5
- 密度 [g/cm3]: 0.915
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.915 g/cc | 0.0331 lb/in³ | ASTM D792 |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 3.5 g/10 min | 3.5 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 8.96 MPa | 1300 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 8.41 MPa | 1220 psi | ASTM D882 |
| Film Elongation at Break, MD | 450 % | 450 % | ASTM D882 |
| Film Elongation at Break, TD | 650 % | 650 % | ASTM D882 |
| Elongation at Break | 300 % | 300 % | on-pallet testing determined by LANTECH SHS Tester: Ultimate Stretch; Dow Method |
| Impact | 10 | 10 | [lbf]; Puncture Resistance Force; Dow Method |
| 49 | 49 | [N]; Puncture at 250% pre-stretch; on-pallet testing determined by LANTECH SHS Tester; Dow Method | |
| 323 | 323 | [ft-lbf/in3]; Puncture Resistance; Dow Method | |
| Puncture Energy | 4.07 J | 3.00 ft-lb | Dow Method |
| Elmendorf Tear Strength MD | 390 g | 390 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 600 g | 600 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 19.19 g/micron | 487.5 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 29.5 g/micron | 750 g/mil | ASTM D1922 |
| Dart drop Test | 630 g | 1.39 lb | Method B; ASTM D1709 |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 35.9 MPa | 5200 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 123 °C | 253 °F | Dow Method (DSC) |
| Vicat Softening Point | 99.0 °C | 210 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 0.60 % | 0.60 % | ASTM D1003 |
| Gloss | 96 % | 96 % | 45°; ASTM D2457 |