- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.935
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in³ | ASTM D792 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 15.23 MPa | 2209 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 16.72 MPa | 2425 psi | ASTM D882 |
| Film Elongation at Break, MD | 522 % | 522 % | ASTM D882 |
| Film Elongation at Break, TD | 656 % | 656 % | ASTM D882 |
| Secant Modulus, MD | 0.377343 GPa | 54.7298 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.348475 GPa | 50.5428 ksi | 2% Secant; ASTM D882 |
| Impact | 93 | 93 | [ft-lbf/in3]; Puncture Resistance; Dow Method |
| 1178 | 1178 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| 1389 | 1389 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 71 g | 71 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 413 g | 413 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 2.80 g/micron | 71.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 16.3 g/micron | 413 g/mil | ASTM D1922 |
| Dart drop Test | 112 g | 0.247 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 38.34 MPa | 5561 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 33.13 MPa | 4805 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126 °C | 259 °F | Dow Method (DSC) |
| Vicat Softening Point | 120 °C | 248 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 7.0 % | 7.0 % | ASTM D1003 |
| Gloss | 58 % | 58 % | 45°; ASTM D2457 |