- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.922
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | ASTM D792 |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Antiblock Level | 3000 ppm | 3000 ppm | |
| Slip Level | 1200 ppm | 1200 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.75 MPa | 1849 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 13.07 MPa | 1895 psi | ASTM D882 |
| Film Elongation at Break, MD | 480 % | 480 % | ASTM D882 |
| Film Elongation at Break, TD | 749 % | 749 % | ASTM D882 |
| Secant Modulus, MD | 0.226658 GPa | 32.8745 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.247074 GPa | 35.8356 ksi | 2% Secant; ASTM D882 |
| Impact | 138 | 138 | [ft-lbf/in3]; Puncture Resistance; Dow Method |
| 2906 | 2906 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| 3671 | 3671 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 435 g | 435 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 576 g | 576 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 21.407 g/micron | 543.75 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 28.3 g/micron | 720 g/mil | ASTM D1922 |
| Dart drop Test | 134 g | 0.295 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 60.43 MPa | 8764 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 49.2 MPa | 7130 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 122 °C | 252 °F | Dow Method (DSC) |
| Vicat Softening Point | 104 °C | 219 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 7.0 % | 7.0 % | ASTM D1003 |
| Gloss | 70 % | 70 % | 45°; ASTM D2457 |