- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.89 MPa | 1579 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 12.29 MPa | 1783 psi | ASTM D882 |
| Film Elongation at Break, MD | 827 % | 827 % | ASTM D882 |
| Film Elongation at Break, TD | 889 % | 889 % | ASTM D882 |
| Secant Modulus, MD | 0.194432 GPa | 28.2004 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.232622 GPa | 33.7395 ksi | 2% Secant; ASTM D882 |
| Impact | 235 | 235 | [ft-lbf/in3]; Puncture Resistance; Dow Method |
| 4176 | 4176 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| 4241 | 4241 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 902 g | 902 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 1200 g | 1200 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 17.8 g/micron | 451 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 23.6 g/micron | 600 g/mil | ASTM D1922 |
| Dart drop Test | 288 g | 0.635 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 55.11 MPa | 7993 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 49.81 MPa | 7224 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 122 °C | 252 °F | Dow Method (DSC) |
| Vicat Softening Point | 108 °C | 226 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 10 % | 10 % | ASTM D1003 |
| Gloss | 60 % | 60 % | 45°; ASTM D2457 |