- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.9175
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9175 g/cc | 0.03315 lb/in³ | ASTM D792 |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Antiblock Level | 2500 ppm | 2500 ppm | |
| Slip Level | 1000 ppm | 1000 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 8.267 MPa | 1199 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 8.811 MPa | 1278 psi | ASTM D882 |
| Film Elongation at Break, MD | 572 % | 572 % | ASTM D882 |
| Film Elongation at Break, TD | 612 % | 612 % | ASTM D882 |
| Secant Modulus, MD | 0.180856 GPa | 26.2314 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.204436 GPa | 29.6515 ksi | 2% Secant; ASTM D882 |
| Impact | 18 | 18 | [lbf]; Puncture Resistance Force; Dow Method |
| 168 | 168 | [ft-lbf/in3]; Puncture Resistance; Dow Method | |
| Puncture Energy | 5.76 J | 4.25 ft-lb | Dow Method |
| Elmendorf Tear Strength MD | 780 g | 780 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 975 g | 975 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 15.4 g/micron | 390 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 19.19 g/micron | 487.5 g/mil | ASTM D1922 |
| Dart drop Test | >= 850 g | >= 1.87 lb | Method B; ASTM D1709 |
| Film Tensile Strength at Break, MD | 38.04 MPa | 5517 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 36.54 MPa | 5299 psi | ASTM D882 |
| Heat Seal Strength Initiation Temperature | 95.0 °C | 203 °F | 2 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 123 °C | 253 °F | Dow Method (DSC) |
| Vicat Softening Point | 100 °C | 212 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 13 % | 13 % | ASTM D1003 |
| Gloss | 64 % | 64 % | 45°; ASTM D2457 |