Dow TUFLIN™ HS-7028 NT 7 Linear Low Density Polyethylene Resin

Dow TUFLIN™ HS-7028 NT 7 Linear Low Density Polyethylene Resin 物性表: Dow TUFLIN™ HS-7028 NT 7 Linear Low Density Polyethylene Resin物性表及特性介绍,Dow TUFLIN™ HS-7028 NT 7 Linear Low Density Polyethylene Resin注塑参数详情,如需Dow TUFLIN™ HS-7028 NT 7 Linear Low Density Polyethylene Resin下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 1.0
  • 密度 [g/cm3]: 0.918
 
Physical PropertiesMetricEnglishComments
Density 0.918 g/cc0.0332 lb/in³ASTM D792
Thickness 20.3 microns0.800 mil
Melt Flow 1.0 g/10 min
@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min
@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
 
Mechanical PropertiesMetricEnglishComments
Film Tensile Strength at Yield, MD 15.98 MPa2318 psiASTM D882
Film Tensile Strength at Yield, TD 15.42 MPa2237 psiASTM D882
Film Elongation at Break, MD 577 %577 %ASTM D882
Film Elongation at Break, TD 800 %800 %ASTM D882
Secant Modulus, MD 0.20403 GPa29.592 ksi2% Secant; ASTM D882
Secant Modulus, TD 0.233243 GPa33.8295 ksi2% Secant; ASTM D882
Impact 9.09.0[lbf]; Puncture Resistance Force; Dow Method
 253253[ft-lbf/in3]; Puncture Resistance; Dow Method
 35643564[ft-lbf/in3]; Toughness MD; ASTM D882
 41184118[ft-lbf/in3]; Toughness TD; ASTM D882
Puncture Energy 3.39 J2.50 ft-lbDow Method
Elmendorf Tear Strength MD 296 g296 gMethod B; ASTM D1922
Elmendorf Tear Strength TD 674 g674 gMethod B; ASTM D1922
Elmendorf Tear Strength, MD 14.6 g/micron370 g/milASTM D1922
Elmendorf Tear Strength, TD 33.17 g/micron842.5 g/milASTM D1922
Dart drop Test 94.0 g0.207 lbMethod A; ASTM D1709
 <= 100 g<= 0.221 lbMethod B; ASTM D1709
Film Tensile Strength at Break, MD 60.68 MPa8801 psiASTM D882
Film Tensile Strength at Break, TD 48.17 MPa6987 psiASTM D882
Heat Seal Strength, Ultimate 9.80 N2.20 lb (f)at 150°C, 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method
Heat Seal Strength Initiation Temperature 110 °C230 °F1 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method
 
Thermal PropertiesMetricEnglishComments
Melting Point 124 °C255 °FDow Method (DSC)
Vicat Softening Point 103 °C217 °FASTM D1525
 
Optical PropertiesMetricEnglishComments
Haze 12 %12 %ASTM D1003
Gloss 50 %50 %45°; ASTM D2457
 62 %62 %20°; ASTM D2457

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-40089.html

免责声明: 本文 Dow TUFLIN™ HS-7028 NT 7 Linear Low Density Polyethylene Resin 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4