- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.17 MPa | 1765 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.02 MPa | 1599 psi | ASTM D882 |
| Film Elongation at Break, MD | 701 % | 701 % | ASTM D882 |
| Film Elongation at Break, TD | 845 % | 845 % | ASTM D882 |
| Secant Modulus, MD | 0.199417 GPa | 28.9234 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.183366 GPa | 26.5954 ksi | 2% Secant; ASTM D882 |
| Impact | 16 | 16 | [lbf]; Puncture Resistance Force; Dow Method |
| 157 | 157 | [ft-lbf/in3]; Puncture Resistance; Dow Method | |
| 3057 | 3057 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| 3496 | 3496 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| Puncture Energy | 5.08 J | 3.75 ft-lb | Dow Method |
| Elmendorf Tear Strength MD | 823 g | 823 g | Method B; ASTM D1922 |
| Elmendorf Tear Strength TD | 1205 g | 1205 g | Method B; ASTM D1922 |
| Elmendorf Tear Strength, MD | 16.20 g/micron | 411.5 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 23.72 g/micron | 602.5 g/mil | ASTM D1922 |
| Dart drop Test | 132 g | 0.291 lb | Method A; ASTM D1709 |
| 270 g | 0.595 lb | Method B; ASTM D1709 | |
| Film Tensile Strength at Break, MD | 40.80 MPa | 5918 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 46.91 MPa | 6803 psi | ASTM D882 |
| Heat Seal Strength, Ultimate | 20.5 N | 4.61 lb (f) | at 150°C, 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Heat Seal Strength Initiation Temperature | 120 °C | 248 °F | 1 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 124 °C | 255 °F | Dow Method (DSC) |
| Vicat Softening Point | 103 °C | 217 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 18 % | 18 % | ASTM D1003 |
| Gloss | 61 % | 61 % | 45°; ASTM D2457 |
| 90 % | 90 % | 20°; ASTM D2457 | |