- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.93
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ASTM D792 |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Antiblock Level | 6000 ppm | 6000 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 15.2 MPa | 2210 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 16.35 MPa | 2372 psi | ASTM D882 |
| Film Elongation at Break, MD | 740 % | 740 % | ASTM D882 |
| Film Elongation at Break, TD | 849 % | 849 % | ASTM D882 |
| Secant Modulus, MD | 0.28989 GPa | 42.046 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.321889 GPa | 46.6867 ksi | 2% Secant; ASTM D882 |
| Impact | 15 | 15 | [lbf]; Puncture Resistance Force; Dow Method |
| 85 | 85 | [ft-lbf/in3]; Puncture Resistance; Dow Method | |
| 4075 | 4075 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| 4315 | 4315 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| Puncture Energy | 3.16 J | 2.33 ft-lb | Dow Method |
| Elmendorf Tear Strength MD | 586 g | 586 g | Method B; ASTM D1922 |
| Elmendorf Tear Strength TD | 1326 g | 1326 g | Method B; ASTM D1922 |
| Elmendorf Tear Strength, MD | 11.5 g/micron | 293 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 26.1 g/micron | 663 g/mil | ASTM D1922 |
| Dart drop Test | <= 100 g | <= 0.221 lb | Method B; ASTM D1709 |
| 166 g | 0.366 lb | Method A; ASTM D1709 | |
| Film Tensile Strength at Break, MD | 53.39 MPa | 7744 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 47.46 MPa | 6884 psi | ASTM D882 |
| Heat Seal Strength, Ultimate | 25.8 N | 5.80 lb (f) | at 170°C, 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Heat Seal Strength Initiation Temperature | 130 °C | 266 °F | 1 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126 °C | 259 °F | Dow Method (DSC) |
| Vicat Softening Point | 114 °C | 237 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 21 % | 21 % | ASTM D1003 |
| Gloss | 26 % | 26 % | 20°; ASTM D2457 |
| 44 % | 44 % | 45°; ASTM D2457 | |