- 熔体流动速率 [g/10min]: 0.5
- 密度 [g/cm3]: 0.932
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.932 g/cc | 0.0337 lb/in³ | ASTM D792 |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.50 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Antiblock Level | 3500 ppm | 3500 ppm | |
| Slip Level | 1200 ppm | 1200 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 25.10 MPa | 3641 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 25.75 MPa | 3735 psi | ASTM D882 |
| Film Elongation at Break, MD | 530 % | 530 % | ASTM D882 |
| Film Elongation at Break, TD | 716 % | 716 % | ASTM D882 |
| Secant Modulus, MD | 0.299805 GPa | 43.4837 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.315559 GPa | 45.7687 ksi | 2% Secant; ASTM D882 |
| Impact | 9.0 | 9.0 | [lbf]; Puncture Resistance Force; Dow Method |
| 158 | 158 | [ft-lbf/in3]; Puncture Resistance; Dow Method | |
| 4414 | 4414 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| 5723 | 5723 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| Puncture Energy | 2.15 J | 1.58 ft-lb | Dow Method |
| Elmendorf Tear Strength MD | 332 g | 332 g | Method B; ASTM D1922 |
| Elmendorf Tear Strength TD | 599 g | 599 g | Method B; ASTM D1922 |
| Elmendorf Tear Strength, MD | 16.3 g/micron | 415 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 29.478 g/micron | 748.75 g/mil | ASTM D1922 |
| Dart drop Test | <= 100 g | <= 0.221 lb | Method B; ASTM D1709 |
| 126 g | 0.278 lb | Method A; ASTM D1709 | |
| Film Tensile Strength at Break, MD | 78.414 MPa | 11373 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 75.470 MPa | 10946 psi | ASTM D882 |
| Heat Seal Strength, Ultimate | 12.9 N | 2.90 lb (f) | at 150°C, 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Heat Seal Strength Initiation Temperature | 120 °C | 248 °F | 1 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126 °C | 259 °F | Dow Method (DSC) |
| Vicat Softening Point | 119 °C | 246 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 13 % | 13 % | ASTM D1003 |
| Gloss | 46 % | 46 % | 20°; ASTM D2457 |
| 49 % | 49 % | 45°; ASTM D2457 | |