- 熔体流动速率 [g/10min]: 58.0
- 密度 [g/cm3]: 0.925
- 缺口冲击强度: 45.0
- 拉伸强度 [MPa]: 10.8
- 弯曲强度 [MPa]: 9.4
- 弯曲模量 [MPa]: 0.380
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | |
| Viscosity | 35000 cP @Shear Rate 5000 1/s, Temperature 190 °C | 35000 cP @Shear Rate 5000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity |
| 60000 cP @Shear Rate 1000 1/s, Temperature 190 °C | 60000 cP @Shear Rate 1000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| 73000 cP @Shear Rate 300 1/s, Temperature 190 °C | 73000 cP @Shear Rate 300 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| Melt Flow | 58 g/10 min @Load 2.16 kg | 58 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 6.8. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 9.40 MPa | 1360 psi | |
| Tensile Strength, Yield | 10.8 MPa | 1570 psi | |
| Elongation at Break | 910 % | 910 % | |
| Modulus of Elasticity | 0.210 GPa | 30.5 ksi | Molded Sample 2% Secant Modulus |
| Flexural Modulus | 0.380 GPa | 55.1 ksi | |
| Izod Impact, Notched (ISO) | 45.0 kJ/m² @Temperature -50.0 °C | 21.4 ft-lb/in² @Temperature -58.0 °F | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 97.2 °C | 207 °F | |