- 熔体流动速率 [g/10min]: 0.95
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | |
| Thickness | 25.0 microns | 0.984 mil | |
| Melt Flow | 0.95 g/10 min @Load 2.16 kg | 0.95 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 8. |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.90 MPa | 1440 psi | |
| Film Tensile Strength at Yield, TD | 10.1 MPa | 1460 psi | |
| Film Elongation at Break, MD | 540 % | 540 % | |
| Film Elongation at Break, TD | 680 % | 680 % | |
| Secant Modulus, MD | 0.146 GPa | 21.2 ksi | Film value |
| Secant Modulus, TD | 0.1545 GPa | 22.41 ksi | Film value |
| Elmendorf Tear Strength MD | 350 g | 350 g | |
| Elmendorf Tear Strength TD | 665 g | 665 g | |
| Elmendorf Tear Strength, MD | 14.0 g/micron | 356 g/mil | |
| Elmendorf Tear Strength, TD | 26.6 g/micron | 676 g/mil | |
| Dart Drop | 29.0 g/micron | 737 g/mil | |
| Film Tensile Strength at Break, MD | 58.0 MPa | 8410 psi | |
| Film Tensile Strength at Break, TD | 46.0 MPa | 6670 psi | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 224 °C | 435 °F | Film extrusion temperature |